One-pot synthesis of bifunctional polyhedral oligomeric silsesquioxane: Full spectrum ratio of vinyl groups from 0 to 100%

Water-based chloroprene latex is a solvent-free, environmentally friendly adhesive. Currently, its market demand is growing rapidly. However, there are problems such as a lack of heat resistance and poor mechanical properties, which limit its application. The introduction of vinyl-POSS (OVS) into the resin structure can effectively improve the thermal stability of chloroprene adhesives. In this paper, modified waterborne chloroprene latex was prepared by copolymerization of methyl methacrylate and OVS with chloroprene latex. The results showed that vinyl-POSS was successfully grafted onto the main chain of the waterborne chloroprene latex, and the modified waterborne chloroprene latex had good storage stability. With the increase in vinyl-POSS, the tensile strength of the chloroprene latex firstly increased and then decreased, the tensile property (peel strength of 20.2 kgf) was maintained well at a high temperature (100 °C), and the thermal stability of the chloroprene latex was improved. When the addition amount was 4%, the comprehensive mechanical properties were their best. This study provides a new idea for the construction of a new and efficient waterborne chloroprene latex system and provides more fields for the practical application of waterborne chloroprene latex. This newly developed vinyl-POSS modified chloroprene latex has great application potential for use in home furniture, bags, and seat cushions.

Section: Introductionmentioning

confidence: 99%

Preparation and Characterization of Chloroprene Latexes Modified with Vinyl-POSS

Chen,

Wu,

Wang

et al. 2024

Improvement of Heat Resistance of Fluorosilicone Rubber Employing Vinyl-Functionalized POSS as a Chemical Crosslinking Agent

Lee

Kim

et al. 2023

Fluorosilicone rubber (F-LSR) is a promising material that can be applied in various cutting-edge industries. However, the slightly lower thermal resistance of F-LSR compared with that of conventional PDMS is difficult to overcome by applying nonreactive conventional fillers that readily agglomerate owing to their incompatible structure. Polyhedral oligomeric silsesquioxane with vinyl groups (POSS-V) is a suitable material that may satisfy this requirement. Herein, F-LSR-POSS was prepared using POSS-V as a chemical crosslinking agent chemically bonded with F-LSR through hydrosilylation. All F-LSR-POSSs were successfully prepared and most of the POSS-Vs were uniformly dispersed in the F-LSR-POSSs, as confirmed by Fourier transform infrared spectroscopy (FT-IR), proton nuclear magnetic resonance spectroscopy (1H-NMR), scanning electron microscopy (SEM), and X-ray diffraction (XRD) measurements. The mechanical strength and crosslinking density of the F-LSR-POSSs were determined using a universal testing machine (UTM) and dynamic mechanical analysis (DMA), respectively. Finally, differential scanning calorimetry (DSC) and thermogravimetric analysis (TGA) measurements confirmed that the low-temperature thermal properties were maintained, and the heat resistance was significantly improved compared with conventional F-LSR. Eventually, the poor heat resistance of the F-LSR was overcome with three-dimensional high-density crosslinking by introducing POSS-V as a chemical crosslinking agent, thereby expanding the potential fluorosilicone applications.

Controlled Surface Textures of Elastomeric Polyurethane Janus Particles: A Comprehensive Review

Trindade

2024

Colloidal particle research has witnessed significant advancements in the past century, resulting in a plethora of studies, novel applications, and beneficial products. This review article presents a cost-effective and low-tech method for producing Janus elastomeric particles of varied geometries, including planar films, spherical particles, and cylindrical fibers, utilizing a single elastomeric material and easily accessible chemicals. Different surface textures are attained through strain application or solvent-induced swelling, featuring well-defined wavelengths ranging from sub-microns to millimeters and offering easy adjustability. Such versatility renders these particles potentially invaluable for medical applications, especially in bacterial adhesion studies. The coexistence of “young” regions (smooth, with a small surface area) and “old” regions (wrinkled, with a large surface area) within the same material opens up avenues for biomimetic materials endowed with additional functionalities; for example, a Janus micromanipulator where micro- or nano-sized objects are grasped and transported by an array of wrinkled particles, facilitating precise release at designated locations through wrinkle pattern adjustments. This article underscores the versatility and potential applications of Janus elastomeric particles while highlighting the intriguing prospects of biomimetic materials with controlled surface textures.