One-step synthesis of fine SrTiO3 particles using SrSO4 ore under alkaline hydrothermal conditions

Preparation of Selected Ceramic Compounds by Controlled Crystallization Under Hydrothermal Conditions

“…EDX spectra obtained on both particles did not show a marked difference on the molar Sr/Ti ratio, because the particles contain similar Sr and Ti amounts as it is suggested by the corresponding EDX spectrum in Fig. 5c ( Rangel-Hernandez et. al., 2009).…”

“…The vessel was heated at a constant rate of 20 ºC/min up at various temperatures (350-500 ºC) for a reaction interval between 0.5 and 2 h. After the treatments, the precipitates were well washed with distilled water, decanted and then dried in an oven at 100 ºC overnight (Rivas-Vázquez et. al., 2004Rendón-Angeles et. al., 2009).…”

Determinación de la variación de los parámetros críticos del compuesto superconductor CaLaBaCu3-xCoxO7-δ (x=0, 0.06, 0.12, 0.18, 0.24)

“…De hecho se relaciona con el modo de empaquetamiento de los iones dentro de la celda perovskita; cuando = 1 una celda de simetría cúbica es formada. Alrededor de valores de = 1, la simetría de la perovskita es menor (Rangel, 2009). …”

“…Lo anterior también se conoce como distorsión estructural la cual puede ser en fase o antifase dependiendo de la energía del sistema y que se ilustra en la Figura 4. Finalmente el factor de tolerancia se relaciona con lo anterior como un indicador que muestra la porción de espacio donde la especie A llena los intersticios cubo-octaédricos creados por los arreglos de B con los aniones (Rangel, 2009). …”

“…1 -Sept. 2013-Feb. 2014 140 Facultad de Ciencias e Ingeniería En la Figura 8 se presenta la resistividad residual y la resistividad a 300 K en función de la temperatura. Las dos curvas presentan una dependencia con la temperatura similar para 0<x<0,24.…”