OPTIMASI WAKTU AKTIVASI DAN KARAKTERISASI ARANG AKTIF DARI BATANG TANAMAN GUMITIR DENGAN AKTIVATOR NaOH

Abstract

The stems of marigold plant can be used as the raw material for making activated carbon. One of the activators that can be used is NaOH with an activated time of 24 hours. The purpose of this study was to obtain an effective activation time through activation with a 2.5% NaOH activator in several variations of activation time followed by characterizing the activated carbon formed. Characterization which was carried out including the determination of water, volatile matter, ash, carbon contents, as well as the absorption capacity of methylene blue and iodine. The results of the study showed that the activation for 28 hours produced an activated carbon with characteristics in accordance with SNI 06-3730-1995, namely: water content (8.40 ± 0.72)%, volatile matter content (9.58 ± 0.95) %, ash content (4.93 ± 0.83)%, carbon content of 77.09%, absorption of iodine (758.66874 ± 1.21) mg/g and absorption of methylene blue 124.6226 mg/g. The results of the analysis with FTIR spectrophotometer on this activated charcoal showed the presence of OH, CH aliphatic, C = O and C = C functional groups.
 
 Keywords: activated carbon, sodium hydroxide, marigold plant stems

Pemanfaatan Karbon dari Bunga Cemara Laut (Casuarina equisetifolia) untuk Penjernihan Minyak Jelantah

“…Selama karbonisasi, bahan volatil dan komponen lain dari bahan dilepaskan dan terbentuk lembaran hidrokarbon aromatik polisiklik yang dikarbonisasi dari biomassa [14]. Jumlah karbon terikat mencerminkan jumlah karbon murni dalam sampel tersebut (Maulana et al, 2017). Nilai karbon terikat dapat dipengaruhi Karbon yang terikat dalam sampel bunga cemara laut bisa berasal dari berbagai komponen organik seperti lignin, selu losa, dan hemiselulosa.…”

Utilization of Borrasus flabellifer L. Palm Coir Activated with Potassium Hydroxide (KOH) as an Efficient Adsorbent for Rhodamine B Dye Removal

“…Wave number 1361─1362 cm -1 indicates the aromatic C-C functional group (Amri et al, 2017). The appearance of the wave number 1034-1033 cm -1 indicates the C-C alkane group, while the wave number 758-761 cm -1 is a group resulting from the vibration (rocking) of the aromatic C-H group (Sahara et al, 2018). The appearance indicates the presence of a C-O ester group (Ariyani et al, 2017).…”

Pemanfaatan Daun Ketapang Sebagai Bio Adsorben Zat Warna Rhodamin B Teraktivasi Asam Sitrat Secara Mechanochemical

“…Sifat higroskopis dapat berpengaruh terhadap kemampuan penyerapan bio adsorben daun ketapang. Semakin tinggi kadar air yang terdapat pada bio adsorben daun ketapang akan mengakibatkan pori-pori akan semakin tertutup oleh air sehingga luas permukaan menjadi kecil dan kemampuan adsorpsinya menjadi berkurang [12,13]. Berdasarkan hasil pengujian kadar air dari sampel daun ketapang dengan variasi waktu aktivasi 30, 45, dan 60 menit disajikan dalam bentuk grafik dapat dapat dilihat pada Gambar 1.…”

“…Hal ini juga terjadi pada penelitian Sahara, dkk. (2020) yang menjelaskan bahwa setelah waktu aktivasi optimum, dinding pori arang aktif mulai erosi atau rusak yang mengakibatkan luas permukaan pori kembali menurun atau mengecil sehingga penyerapan arang berkurang [13]. Hasil analisis daya serap iodium yang memenuhi standar SNI menunjukkan bahwa daun ketapang yang teraktivasi menghasilkan bio adsorben berkualitas baik.…”