Outstanding Piezoelectricity of (K, Na)(Nb, Sb)O3-SrZrO3-(Bi, Ag)ZrO3 Piezoceramics and Their Application to a Planar-Type Actuator

Abstract

Fe2O3-added 0.96(K0.5Na0.5)(Nb0.94Sb0.06)-0.01SrZrO3-0.03(BiAg)ZrO3 [KNNS-0.01SZ-0.03BAZ] piezoceramic was well densified at 1090 °C. It exhibited a large piezoelectric charge constant (d33) of 650 pC/N, which is similar to the largest d33 value reported in the literature. This sample has a tetragonal-orthorhombic-rhombohedral (T-O-R) structure, in which each structure has a similar proportion. Moreover, nanodomains (2 nm × 15 nm) with low domain boundary energy were found in this sample, which exhibited relaxor properties. Therefore, the presence of a T-O-R multi-structure and nanodomains is responsible for the large d33 value of this sample. A KNNS-0.01SZ-0.03BAZ thick film was synthesized, and it also had a T-O-R multi-structure with a large d33 (630 pC/N). A planar-type actuator was produced using this thick film, and this actuator exhibited a large acceleration (335 G at 120 V/mm) and displacement (231 μm at 120 V/mm). Hence, the KNNS-0.01SZ-0.03BAZ thick film is a good candidate for lead-free piezoelectric actuators.