Oxidation Resistance and Bending Strength at High Temperatures of Ni/(ZrO₂+Al₂O₃) Hybrid Materials

Abstract

Oxidation resistance and bending strength at high temperatures of 5 vol% Ni/(10 vol% ZrO2+Al2O3) were investigated in this paper. Oxidation tests were conducted at temperature ranging from 1100 to 1300oC for 1 to 24 h in air. The oxidation resistance of the composites was studied via observation of oxidized-zone development from a cross-section view after oxidation. Three-point bending tests were conducted at temperatures ranging from room temperature to 1200oC in order to estimate its performance at high temperatures. Bending strength of the composites achieved 1200 MPa at room temperature and 460 MPa at 1200oC. Dispersion of ZrO2in Ni/Al2O3composites enhanced both their room and high temperature bending strength. Nevertheless, ZrO2slightly degraded the oxidation resistance of the composites. The oxidation rate of Ni/(ZrO2+Al2O3) was one order of magnitude higher than that of Ni/Al2O3.