Performance Assessment of a Novel Green Concrete Using Coffee Grounds Biochar Waste

Abstract

An actual scientific problem in current concrete science is poor knowledge of the problem of modifying concrete with plant waste. At the same time, plant waste benefits from other types of waste because it is a recycled raw material. A promising technological approach to modifying concrete with plant waste is the introduction of components based on the processing of coffee production waste into concrete. This study aims to investigate the use of biochar additives from spent coffee grounds (biochar spent coffee grounds—BSCG) in the technology of cement composites and to identify rational formulations. A biochar-modifying additive was produced from waste coffee grounds by heat treatment of these wastes and additional mechanical grinding after pyrolysis. The phase composition of the manufactured BSCG additive was determined, which is characterized by the presence of phases such as quartz, cristobalite, and amorphous carbon. The results showed that the use of BSCG increases the water demand for cement pastes and reduces the cone slump of concrete mixtures. Rational dosages of BSCG have been determined to improve the properties of cement pastes and concrete. As a result of the tests, it was determined that the ideal situation is for the BSCG ratio to be at a maximum of 8% in the concrete and not to exceed this rate. For cement pastes, the most effective BSCG content was 3% for concrete (3%–4%). The compressive and flexural strengths of the cement pastes were 6.06% and 6.32%, respectively. Concrete’s compressive strength increased by 5.85%, and water absorption decreased by 6.58%. The obtained results prove the feasibility of using BSCG in cement composite technology to reduce cement consumption and solve the environmental problem of recycling plant waste.