Pitting Corrosion Resistance of CA6NM and 410 Martensitic Stainless Steels in Various Environments

Abstract

Pitting corrosion is an importance phenomena in power generation steam turbine, as it is one of the main causes for blade failure, particularly in the last row of low pressure blading. In this work, the pitting corrosion resistance of the widely used blading alloy of wrought 410 stainless steel and that of the candidate alloy of cast CA6NM stainless steel were investigated. Cyclic polarization measurements for all samples were conducted in simulated solution of thermal and geothermal power plants. The experimental results show that the pitting potentials of the cast CA6NM steel were higher compared to those of the wrought 410 steel in all simulated solution. Both steels exhibited higher pitting potentials in CO2 containing simulated geothermal water than those in the other solutions. These results were correlated with microstructure of the steels observed by Scanning Eectron Microscope (SEM).

The Effect of Ecap Processing to Hardness, Surface Morphologi, and Corrosion Resistance of 6061 Aluminium Alloys

“…Open circuit potential is an important variable to understand the corrosion resistance of materials. The higher value of free corrosion potential indicated the difficulty of material to corrode [21]. According to Table 2, the free corrosion potential value of Al 6061 with four passes has the highest value of all samples.…”