Pitting resistance of 06KhN28MDT alloy in chloride-containing media

Prediction the durability of heat exchangers made of 06KhN28MDT alloy (analogous to AISI904L steel) to crevice corrosion during their operation in recycled water

“…Five industrial melts of the 06KhN28MDT alloy have been studied. Their chemical composition and structural heterogeneity have been determined earlier [10]. The specific magnetic susceptibility of the alloy has been determined in [16].…”

“…After all, they have high corrosion resistance to intercrystalline corrosion in these media [2]. But the circulating water, which is used to cool the technological product during the production of acids, contains chlorides and other anions [3][4][5][6], which can be the cause of pitting or crevice corrosion of heat exchangers [7][8][9][10]. In particular, design features of plate-like heat exchangers and chlorides in circulating water can be the cause of their crevice corrosion between the corrugations of adjacent plates.…”

“…In particular, design features of plate-like heat exchangers and chlorides in circulating water can be the cause of their crevice corrosion between the corrugations of adjacent plates. Today, there are many studies devoted to the assessment and prediction of pitting resistance of steels AISI304 [8], AISI321 [12,13] and alloy 06KhN28MDT [7][8][9][10], which are used in the production of plate-like heat exchangers. In papers [10][11][12], the patterns and mechanisms of the genesis and growth of pitting on their surface in chloridecontaining media have been investigated, in paper…”

Influence of chemical composition and structural heterogeneity of 06ХН28МДТ alloy on mechanisms of its pits formation in return waters

“…Ці результати узгоджуються з даними про анодне селективне розчинення металів і сплавів, які піддавалися загальній корозії [11][12][13][14][15][16][17][18][19][20][21][22][23][24][25][26], але вони також мають характерні для локальних процесів особливості притаманні метастабільним і стабільним пітінгам. Пітінготривкість сплаву 06ХН28МДТ в модельних оборотних водах досліджено в працях [27][28][29][30][31]. У них встановлено залежності між критерієм пітінготривкості сплаву та його хімічним складом і структурою.…”

“…Досліджено п'ять плавок сплаву 06ХН28МДТ. Хімічний склад і структурну гетерогенність визначили раніше [1,3,29,30]. Зразки дослідного сплаву витримували в хлоридовмісних розчинах з pH = 4…8 та концентрацією хлоридів 180 мг/л при температурі 343 К упродовж 240 годин.…”