Preparation and characterization of hydroxyapatite macrobeads based on pneumatic extrusion dripping

Isloor

et al. 2019

Sci Rep

With the continuous quest of developing hydrogel for cartilage regeneration with superior mechanobiological properties are still becoming a challenge. Chitosan (CS) hydrogels are the promising implant materials due to an analogous character of the soft tissue; however, their low mechanical strength and durability together with its lack of integrity with surrounding tissues hinder the load-bearing application. This can be solved by developing a composite chitosan hydrogel reinforced with Hydroxyapatite Nanorods (HANr). The objective of this work is to develop and characterize (physically, chemically, mechanically and biologically) the composite hydrogels loaded with different concentration of hydroxyapatite nanorod. The concentration of hydroxyapatite in the composite hydrogel was optimized and it was found that, reinforcement modifies the hydrogel network by promoting the secondary crosslinking. The compression strength could reach 1.62 ± 0.02 MPa with a significant deformation of 32% and exhibits time-dependent, rapid self-recoverable and fatigue resistant behavior based on the cyclic loading-unloading compression test. The storage modulus value can reach nearly 10 kPa which is needed for the proposed application. Besides, composite hydrogels show an excellent antimicrobial activity against Escherichia coli, Staphylococcus aureus bacteria’s and Candida albicans fungi and their cytocompatibility towards L929 mouse fibroblasts provide a potential pathway to developing a composite hydrogel for cartilage regeneration.

Section: Resultsmentioning

confidence: 95%

Nanohydroxyapatite Reinforced Chitosan Composite Hydrogel with Tunable Mechanical and Biological Properties for Cartilage Regeneration

Isloor

et al. 2019

Sci Rep

“…Typically, extrusion dripping or spring extrusion is used to form alginate beads by extruding the alginate solution with bioactive molecules into a calcium chloride solution. 147 Extrusion has been widely used for encapsulating unstable volatile flavors in a glossy carbohydrate matrix. By using this approach, unstable flavor compounds can be sustained in the glossy matrix with less oxidation to extend shelf life.…”

Section: Encapsulation Technologies To Improve the Stability Of Milk Bioactivesmentioning

confidence: 99%

Bioactives in bovine milk: chemistry, technology, and applications

et al. 2021

The significance of dairy in human health and nutrition is gaining significant momentum as consumers continue to desire wholesome, nutritious foods to fulfill their health and wellness needs. Bovine milk not only consists of all the essential nutrients required for growth and development, it also provides a broad range of bioactive components that play an important role in managing human homeostasis and immune function. In recent years, milk bioactives, including α-lactalbumin, lactoferrin, glycomacropeptide, milk fat globule membrane, and milk oligosaccharides, have been intensively studied because of their unique bioactivity and functionality. Challenges for the application of these bioactive components in food and pharmaceutical formulations are associated with their isolation and purification on an industrial scale and also with their physical and chemical instability during processing, storage, and digestion. These challenges can be overcome by advanced separation techniques and sophisticated nano- or micro-encapsulation technologies. Current knowledge about the chemistry, separation, and encapsulation technology of major bioactives derived from bovine milk and their application in the food industry is reviewed here.

“…HAP can be synthesized by various methods, including sol-gel, wet precipitation, burning in the presence of microwaves and ultrasounds [14][15][16][17][18][19][20][21]. Its slightly alkaline pH and high biocompatibility will not cause any form of secondary environmental damage.…”

mentioning

confidence: 99%

Hydroxyapatite Nanoparticles for Acidic Mine Waters Remediation

Simonescu¹,

Culiță²,

Marinescu³

et al. 2019

Rev. Chim.

Mining activities have a high negative impact on the environment and on human health. Environmental impacts can result in contamination of surface water, groundwater, soil and air. Large volumes of wastewater produced by mining activities have to be remediated before being discharged into the environment. Due to the complex composition of wastewater coming from the mining industry and because their negative impacts, numerous remediation techniques have been applied. Adsorption is one of the most extensively used ways to remediate mining wastewater as a consequence of its low cost, easiness to be performed, and also due to the wide variety of materials (natural and synthetic) that can be use as adsorbents. Hydroxyapatite (HAP, Ca10(PO4)6(OH)2), a naturally occurring form of calcium phosphate has a good capacity to remove heavy metal ions from aqueous solutions due to its excellent properties. By preparing hydroxyapatite using different synthesis methods, its properties can be manipulated in order to increase the adsorption properties and reactivity. Herein, we reported synthesis of hydroxyapatite (HAP) samples using different synthesis conditions to establish the effect of synthesis conditions onto HAP properties. The HAP samples prepared have been characterized by the use of X-ray diffraction, FT-IR spectroscopy, specific surface measurements, Scanning Electron Microscopy (SEM). The stoichiometric compounds with high degree of crystallinity, low average particle diameter values, and low specific surface have been prepared by the solid state reaction and high calcination temepratures. The addition of surfactant (dispersant) has resulted in an increase in the specific surface area, which will result in an increase in the retention capacity of heavy metal ions in wastewater. The adsorbents prepared were used to remediate mine water. Results showed that non-calcinated HAP samples have a higher heavy metals adsorption capacity compared to HAP samples calcinated at 600 �C and 900 �C. The HAP samples prepared in presence of surfactant exhibit a higher heavy metals adsorption capacity than samples prepared in absence of surfactant. The values of the retention capacity differ depending on the nature of the metal ion: QMn(II) ] QFe(III) ] QZn(II) ] QPb(II) ] QNi(II). A change in the pH of mine water from 2.6 to 5.5 has occur that means that the metal ion retention mechanism goes through chemical reactions. The metal ions retention capacity suggests application of hydroxyapatite for remediation of mining wastewater.