Preparation and dielectric properties of Ba((Fe<inf>0.5</inf>Nb<inf>0.5</inf>)O<inf>3</inf>/Al<inf>2</inf>O<inf>3</inf> composite ceramics with core/shell structure

Abstract

Aluminum oxide (Al 2 O 3 ) coated Ba(Fe 0.5 Nb 0.5 )O 3 (BFN) particles (abbreviated as BFN/Al 2 O 3 ) were synthesized using a facile chemical method. BFN and BFN/Al 2 O 3 ceramic samples were sintered at 1350 and 1200 for 3 h, respectively. The microstructure and dielectric properties of Al 2 O 3 modified BFN ceramics were investigated by transmission electron microscopy (TEM), scanning electron microscopy (SEM) and dielectric measurements. Core/shell structure of BFN/Al 2 O 3 composite was achieved and the Al 2 O 3 is amorphous while BFN/Al 2 O 3 composite powders were treated at 800 for 2 h. The grain sizes of BFN/Al 2 O 3 composite ceramic were obviously smaller than those of pure BFN ceramics. The dielectric constant still maintained a large value, and the temperature stability of the ceramics has been improved significantly with coating Al 2 O 3 layer. The dielectric loss of BFN/Al 2 O 3 composite ceramics was lower than that of BFN ceramics especially in high temperature range. The enhancement of the insulation intensity of grain boundaries and smaller grain sizes derived from the core/shell structure played important roles to reduce the dielectric loss of the BFN ceramics. Index Terms-composite, core/shell structure, Ba(Fe 0.5 Nb 0.5 )O 3 , dielectric.