Properties of mullite-zirconium ceramic obtained by spark plasma sintering

Dense mullite zirconia composites obtained from the reaction sintering of milled stoichiometric alumina zircon mixtures by SPS

“…For the mullite-zirconia composites without sintering additives, the mullite formation was accomplished at 1540 1C, this temperature was lowered by the employed additives. Clay was employed as sintering additive for this kind of material with good results but with the disadvantage of incorporation of impurities [25].…”

Sintering a mixture of powders in the Al2O3-SiO2-P-SiAlON-TiC-Dy2O3 system by the plasma-spark method with the high compaction load

“…В силу вышеуказанных причин в плазменноискровом спекании, аналогично традиционному спеканию смеси оксидных порошков [7], используют добавки оксидных порошков (Y 2 O 3 , Yb 2 O 3 , Gd 2 O 3 , Dy 2 O 3 ), формирующие с оксидным и безоксидным порошками легкоплавкие эвтектики и твердые растворы в виде стабильных в твердой фазе или нестабильных в жидкой фазе соединений [8][9][10][11][12]. Использование данного вида спекания и оксидных добавок с малыми катионными радиусами металлов наиболее стимулирует диффузию (внедрение) соответствующих катионов металлов в структуру исходных компонентов с активным образованием твердого раствора в твердой фазе [8,9], который формируется также через образование и распад соединений разной стехиометрии в твердой фазе [8,9].…”