Propriétés viscoélastiques de la poly(α,α‐diéthyl‐β‐propiolactone)

Abstract

The viscoelastic properties of poly(a,a-diethyl-/3-propiolactone) were investigated in the linear range using stress relaxation and dynamic mechanical methods. Using Ferry's reduction method, a horizontal shift factor was determined at each temperature, that satisfactorily agreed with the WLF equation in the transition zone. No vertical shift was required to superimpose different relaxation curves. The apparent activation energy was temperature dependent and passed through a maximum near Tg whose value is (31 1 + 2) K. The relaxation spectrum has been calculated according to the first method of approximation of Schwarzl and Staverman. It consists of a high intensity plateau at shorter times, a wedge type portion with a slope of -0,15 and a low intensity plateau at longer times. Dynamical mechanical measurements revealed a p relaxation peak at 333 K and yielded the evidence of a y peak around 120 K. a) Poly(oxydimtthyl-2,2 0x0-1 trimkthylhe). b, Poly(oxydiL.thy1-2,2 0x0-1 trimtthylhe).