Pure and fully texturized Sr2FeMoO6 thin films prepared by pulsed laser deposition from target made with citrate-gel method

The effect of film thickness on the magnetic and magneto-transport properties of Sr2FeMoO6thin films

“…In order to reach applications which operate at room temperature, the fabrication of high quality thin films with T C clearly over room temperature is necessary. Even though the properties of SFMO are excellent for these applications, the fabrication of SFMO thin films has proven to be difficult [5][6][7]. The challenges in the SFMO thin film fabrication are due to extreme preparation conditions and easily formed impurity phases [5,6,[8][9][10].…”

“…Even though the properties of SFMO are excellent for these applications, the fabrication of SFMO thin films has proven to be difficult [5][6][7]. The challenges in the SFMO thin film fabrication are due to extreme preparation conditions and easily formed impurity phases [5,6,[8][9][10]. The best method to achieve pure and fully textured SFMO films has proven to be pulsed laser deposition (PLD) [5,6,11], because it does not require such a high vacuum and a stoichiometric target can be used.…”

“…The challenges in the SFMO thin film fabrication are due to extreme preparation conditions and easily formed impurity phases [5,6,[8][9][10]. The best method to achieve pure and fully textured SFMO films has proven to be pulsed laser deposition (PLD) [5,6,11], because it does not require such a high vacuum and a stoichiometric target can be used. Earlier we have reported SFMO thin films with no indication of different orientations or impurity phases made with PLD in Ar/H 2 (5%) atmosphere and at 1050…”

Phase Transformations and Magnetic State in the Nanoscale Metal-Oxide Sr$_{2}$FeMoO$_{6-\delta}$ Compounds

“…При отсутствии точечных дефектов, идеальная структура имеет длинноцепочечное сверх-структурное упорядочение (Р) катионов -Fe 3 -О 2 -Mo 5 -с высо-кими значениями величины намагниченности насыщения (MS), приближающейся к теоретической 4,0 B /ф.е. Уменьшение MS сви-детельствует о наличие антиструктурных дефектов типа FeMo, MoFe [7], а теоретические расчёты, проведённые в работах [8][9][10][11], предсказывают возможность появления антиферромагнитного упо-рядочения в цепочках Fe-O-Fe и парамагнитного в цепочках Mo-O-Mo.…”

“…Практическая трудность регулировки концентрации дефектов кристаллической структуры и их упорядочения связана со сложно-стью и многостадийностью химических реакций, протекающих при кристаллизации Sr 2 FeMoO 6 , низкой кинетикой фазообразования и слабой подвижностью катионов Fe и Mo [7,11,18,20]. В связи с этим в последнее время учёные все больше начинают прибегать к золь-гель-технологии, обладающей большими потенциальными возможностями, позволяющей синтезировать наноразмерный двойной перовскит при сравнительно невысокой температуре и меньших затратах времени [13,14,21].…”