Relationship between Chemical Bonding Nature and Electrochemical Property of LiMn₂O₄ Spinel Oxides with Various Particle Sizes:  “Electrochemical Grafting” Concept

Abstract

Systematic Mn 2p XPS and Mn K-edge XAS analyses together with the electrochemical measurement have been carried out for the spinel LiMn 2 O 4 prepared at various sintering temperatures in order to elucidate an origin of the dependence of electrochemical properties on synthetic conditions. From the comparative experiments, it becomes clear that a lowering of synthetic temperature gives rise to an increase of structural disorder and of the average oxidation state of manganese, which is more prominent on the surface than in the bulk. Such results suggest that the modification of surface property induced by a decrease of particle size is closely related to the electrochemical performance. The nanocrystalline LiMn 2 O 4 prepared at 250 °C shows excellent cyclability at the 3 V region compared to that of microcrystalline LiMn 2 O 4 prepared at 700 °C. For the purpose of examining the evolution of the chemical bonding nature of inserted lithium, 7 Li MAS NMR studies have been performed for both the spinel compounds before and after Li + intercalation. While the intercalation of 0.2 mol Li + does not induce any remarkable spectral change for the microcrystalline LiMn 2 O 4 , it leads to a dramatic suppression of the NMR signal for the nanocrystalline LiMn 2 O 4 , indicating that the process of grafting Li into the latter phase results in significant modifications of the chemical environment of lithium. On the basis of present experimental findings, it can be concluded that the lowering of synthetic temperature modifies the surface properties, which facilitates the grafting process of Li + ion and, thereby, enhances the electrochemical properties for the 3 V region corresponding to the Li insertion.

Unique Properties of 2 D Layered Titanate Nanosheets as a Building Block for the Optimization of the Photocatalytic Activity and Photostability of TiO2‐Based Nanohybrids

“…[31] As shown in the left panel of Figure 4, the hybridization with TiO 2 2D nanosheets leads to a marked shift of Ag 3d peak toward higher energy side. In contrast to all other elements, Ag shows very unique opposite trend in the energy shift of XPS peak upon the variation of oxidation state; a decrease of Ag oxidation state from Ag + to Ag 0 gives rise to an increase of the binding energy (BE) of Ag 3d XPS peak.…”

Study of the lithium insertion–deinsertion mechanism in nanocrystalline γ-Fe2O3 electrodes by means of electrochemical impedance spectroscopy

“…It is divided in two steps (process (1), Fig. 1), the first one occurring at/near the grain interface is concomitant to the electron filling of these cationic sub-band gap energy states and maintains the electroneutrality [17]. It leads to a monotonous discharge in the first part of the curve as compared to the well-crystalline homologues.…”

Manganese dissolution from LiMn2O4 cathodes at elevated temperature: methylene methanedisulfonate as electrolyte additive

“…The step in the Li + charge-transfer process is a subject of interest for improving the rate performance. There are Mn 3+ (641.7 eV), Mn 4+ (642.9 eV), and Mn 2p 1/2 (653.6 eV) peaks in Mn 2p spectra [37]. Both the peak position and the intensity ratio of Mn 2p 3/2 and Mn 2p 1/2 showed that the LiMn 2 O 4 existed in a stoichiometric spinel form [16].…”