“…Fouling appearance is inevitable in membrane processes, as it decreases water productivity, deteriorates permeate quality, and shortens membrane lifespan [ 2 , 3 , 4 , 5 ]. Fouling level and types depend on membrane operational factors, hydrodynamic conditions and membrane characteristics [ 6 ].…”
Polysulfone (PSU) film and N-vinylimidazole (VIM) were used to obtain grafted membranes with high hydrophilic capacity. The grafting process was performed by gamma irradiation under two experiments: (1) different irradiation doses (100–400 kGy) and VIM 50% solution; (2) different concentration of grafted VIM (30–70%) and 300 kGy of irradiation dose. Characteristics of the grafted membranes were determined by Fourier transform infrared spectroscopy (FTIR), scanning electron microscopy (SEM), contact angle, swelling degree, desalination test, thermogravimetric analysis (TGA) and differential scanning calorimetry (DSC). Both experiments indicated that the absorbed dose 300 kGy and the VIM concentration, at 50% v/v, were effective to obtain PSU grafted membranes with 14.3% of grafting yield. Nevertheless, experimental conditions, 400 kGy, VIM 50% and 300 kGy, VIM 60–70% promoted possible membrane degradation and VIM homopolymerization on the membrane surface, which was observed by SEM images; meanwhile, 100–200 kGy and VIM 30–50% produced minimal grafting (2 ± 0.5%). Hydrophilic surface of the grafted PSU membranes by 300 kGy and VIM 50% v/v were corroborated by the water contact angle, swelling degree and desalination test, showing a decrease from 90.7° ± 0.3 (PSU film) to 64.3° ± 0.5; an increment of swelling degree of 25 ± 1%, and a rejection-permeation capacity of 75 ± 2%. In addition, the thermal behavior of grafted PSU membranes registered an increment in the degradation of 20%, due to the presence of VIM. However, the normal temperature of the membrane operation did not affect this result; meanwhile, the glass transition temperature (Tg) of the grafted PSU membrane was found at 185.4 ± 0.5 °C, which indicated an increment of 15 ± 1%.
“…Fouling appearance is inevitable in membrane processes, as it decreases water productivity, deteriorates permeate quality, and shortens membrane lifespan [ 2 , 3 , 4 , 5 ]. Fouling level and types depend on membrane operational factors, hydrodynamic conditions and membrane characteristics [ 6 ].…”
Polysulfone (PSU) film and N-vinylimidazole (VIM) were used to obtain grafted membranes with high hydrophilic capacity. The grafting process was performed by gamma irradiation under two experiments: (1) different irradiation doses (100–400 kGy) and VIM 50% solution; (2) different concentration of grafted VIM (30–70%) and 300 kGy of irradiation dose. Characteristics of the grafted membranes were determined by Fourier transform infrared spectroscopy (FTIR), scanning electron microscopy (SEM), contact angle, swelling degree, desalination test, thermogravimetric analysis (TGA) and differential scanning calorimetry (DSC). Both experiments indicated that the absorbed dose 300 kGy and the VIM concentration, at 50% v/v, were effective to obtain PSU grafted membranes with 14.3% of grafting yield. Nevertheless, experimental conditions, 400 kGy, VIM 50% and 300 kGy, VIM 60–70% promoted possible membrane degradation and VIM homopolymerization on the membrane surface, which was observed by SEM images; meanwhile, 100–200 kGy and VIM 30–50% produced minimal grafting (2 ± 0.5%). Hydrophilic surface of the grafted PSU membranes by 300 kGy and VIM 50% v/v were corroborated by the water contact angle, swelling degree and desalination test, showing a decrease from 90.7° ± 0.3 (PSU film) to 64.3° ± 0.5; an increment of swelling degree of 25 ± 1%, and a rejection-permeation capacity of 75 ± 2%. In addition, the thermal behavior of grafted PSU membranes registered an increment in the degradation of 20%, due to the presence of VIM. However, the normal temperature of the membrane operation did not affect this result; meanwhile, the glass transition temperature (Tg) of the grafted PSU membrane was found at 185.4 ± 0.5 °C, which indicated an increment of 15 ± 1%.
“…Sodium carboxymethyl cellulose is a well‐known polyelectrolytic polymer which was deliberately used in this work in order to impart electrical conductivity into the membrane which will enable it to be used in ED‐based applications and addition of polyelectrolytic polymer to the composite bestows good electrical mobility in the polymer. PVP is also known for its hydrophilic quality, thus increasing the water affinity of the membrane . AC due to its high surface area is known a dye adsorbent.…”
“…Polyvinyl pyrrolidone is often used in the microneedle due to its dual role as an additive: (a) increasing the affinity of a matrix to water and (b) acting as a pore-forming agent to improve dissolution profile. 42 Figure 5. Ex vivo polymer dissolution of self-dissolving microneedles (A) UN-1 and (B) UN-2.…”
Acyclovir is an antiviral drug that is frequently prescribed for the herpes virus. However, the drug requires frequent dosing due to limited bioavailability (10–26.7%). The rationale of the present study was to develop a self-dissolving microneedle system for local and systemic delivery of acyclovir using a topical lyophilized wafer on microneedle-treated skin to provide the drug at the site of infection. The microneedles prepared with hydroxypropyl methylcellulose (HPMC) (8% w/w) or HPMC (8% w/w)-polyvinyl pyrrolidone (PVP) (30% w/w) penetrated excised rat skin, showing sufficient mechanical strength and rapid polymer dissolution. The topical wafer was prepared with acyclovir (40% w/w; equivalent to 200 mg of drug), gelatin (10% w/w), mannitol (5% w/w), and sodium chloride (5% w/w). The uniform distribution of acyclovir within the wafer in an amorphous form was confirmed by differential scanning calorimetry (DSC) and thermogravimetric analysis (TGA). No polymer–drug interaction was evident in the lyophilized wafer as per Fourier transform infrared spectroscopy (FTIR) analysis. The wafer showed a sufficiently porous structure for rapid hydration as per scanning electron microscopy (SEM) analysis. During ex-vivo analysis, the skin was pre-treated with a self-dissolving microneedle array for 5 minutes, and the wafer was placed on this microporated-skin. Topical wafer provided ∼7–11 times higher skin concentration than the ID99 reported with a lower lag-time. Based on in-vivo testing, ∼2.58 µg/ml of Cmax was achieved in rabbit plasma during 24 hours’ study. Our findings suggest that the self-dissolving microneedle-assisted topical wafer, proposed for the first time, would be efficacious against the infection residing in the skin layer and for systemic therapy.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.