Role of SiO2 coating in multiferroic CoCr2O4 nanoparticles

Abstract

Effect of silica (SiO2) coating concentration on structural and magnetic properties of multiferroic cobalt chromite (CoCr2O4) nanoparticles have been studied. The nanoparticles with average crystallite size in the range 19 to 28 nm were synthesised by sol-gel method. X-ray diffraction (XRD) analysis has verified the composition of single-phase cubic normal spinel structure of CoCr2O4 nanoparticles. The average crystallite size and cell parameter decreased with increasing SiO2 concentration. TEM image revealed that the shape of nanoparticles was non-spherical. Zero field cooled/field cooled (ZFC/FC) curves revealed that nanoparticles underwent a transition from paramagnetic (PM) state to collinear short-range ferrimagnetic (FiM) state, and this PM–FiM transition temperature decreased from 101 to 95 K with increasing SiO2 concentration or decreasing crystallite size. A conical spin state at Ts = 27 K was also observed for all the samples which decreased with decreasing average crystallite size. Low temperature lock-in transition was also observed in these nanoparticles at 12 K for uncoated nanoparticles which slightly shifted towards low temperature with decreasing average crystallite size. Saturation magnetization (Ms) showed decreasing trend with increasing SiO2 concentration, which was due to decrease in average crystallite size of nanoparticles and enhanced surface disorder in smaller nanoparticles. The temperature dependent AC-susceptibility also showed the decrease in the transition temperature (Tc), broadening of the Tc peak and decrease in magnetization with increasing SiO2 concentration or decreasing average crystallite size. In summary, the concentration of SiO2 has significantly affected the structural and magnetic properties of CoCr2O4 nanoparticles.

Surface driven exchange bias in nanocrystalline CoCr2O4

“…The values of R p , R wp , R F 2 and χ 2 are 0.022 5, 0.030 2, 0.127 5 and 1.151 respectively, which indicate a good matching between the calculated and experimental patterns [29,32]. The XRD pattern is fitted using cubic structure (Fd3m) with a ≈ 8.337 Å, which is in good agreement with the recent results [27,[33][34][35]. The difference plot at the bottom of figure 1 shows a satisfactory matching of the experimental curve with the computed one and the Rietveld analysis confirms the formation of singlephase of the sample and no other oxide phase can be detected from the diffraction plot [11,15,36].…”

Fabrication, characterization, and antibacterial activity of ferrite, chromite, and aluminate nanoparticles

“…The cubic morphology can be attributed to the directed self-assembly growth of NPs which improves the antibacterial property and is then considered as the preferable shape for applications in hyperthermia treatment [57][58][59]. Moreover, it is obvious that the magnetic F and C samples tend to agglomerate due to the magnetic attractions between NPs [60,61]. However, the particles in sample A are well distributed and not agglomerated, which can be related to the presence of MgO secondary phase, as detected by XRD analysis.…”

Role of surface spins on magnetization of Cr2O3 coated γ-Fe2O3 nanoparticles

“…where D is crystallite size, λ is the wavelength having constant value 0.1541 nm, β is the full width at half maxima, K is a shape constant and θ is the diffraction angle [23]. The average crystallite size of γ Fe 2 O 3 nanoparticles is 13 nm.…”