Room-Temperature Extra-huge Magnetoresistance Effect in MnSb Granular Films.

Spintronics: A Challenge for Materials Science and Solid‐State Chemistry

“…Very recently, CrAs and CrSe in the zinc‐blende and wurtzite structures were proposed to be half‐metallic ferromagnets 158. Akinaga et al.…”

“…succeeded in growing thin films of CrAs by using molecular beam epitaxy. They found that the CrAs films, which they assumed to adopt the zinc‐blende structure, are ferromagnetic at room temperature ( T C >400 K), with a saturation moment of 3 μ B 158. Bulk CrAs adopts the MnP structure and exhibits complex magnetic behavior below a transition temperature of 256 K. Bulk samples may also crystallize as Cr 2 As, which is an antiferromagnet with a Néel temperature of 393 K. In good agreement with experiment, spin‐polarized band‐structure calculations demonstrated that ferromagnetic zinc‐blende CrAs should be a half‐metal with a magnetic moment of 3 μ B 159.…”

Spintronik: eine Herausforderung für Materialwissenschaften und Festkörperchemie

“…Leider gibt es aber nur wenige binäre Verbindungen mit magnetischen Elementen, die in der ZnS‐Struktur kristallisieren – kürzlich wurden CrAs und CrSe mit Zinkblende‐ bzw. Wurtzitstruktur als mögliche halbmetallische Ferromagnete vorgeschlagen 158. Akinaga et al.…”

“…Akinaga et al. konnten durch Molekularstrahlepitaxie (MBE) dünne Filme von CrAs herstellen und fanden, dass CrAs bei Raumtemperatur ferromagnetisch mit T C >400 K und einem Gesamtmoment von 3 μ B in Sättigung ist 158. Volumenproben kristallisieren in der MnP‐Struktur mit einem komplexen magnetischen Verhalten und einer Übergangstemperatur von 256 K oder in der Cr 2 As‐Struktur, die antiferromagnetisch ist und eine Néel‐Temperatur von 393 K aufweist.…”