Ti 12x )O 3 (x = 0, 0.05, 0.1, and 0.15, BZT for short) has been prepared using the solid solution reaction from BaTiO 3 (BT) and BaZrO 3 (BZ). For transmission electron microscopy (TEM) analysis, the cubic phase of BZT coexists with the tetragonal one in the Ba(Zr 0.15 Ti 0.85 )O 3 ceramics. Its structure of ceramics has been estimated using the Rietveld and Cohen methods. The effect of BaZrO 3 content on the tetragonality of BZT and its relation to a dielectric constant have been studied, and it is found that the tetragonality approaches 1 as the BZ content is increased, while simultaneously the Curie temperature of BZT decreases at a rate of 4.66°C per mole pct BZ. The average grain size was sensitive to the BZ content, and the P r could be enhanced at room temperature.