Strengthening Thermal Stability in V2O5-ZnO-BaO-B2O3-M(PO3)n Glass System (M = Al, Mg) for Laser Sealing Applications

Abstract

Today, the most common way of laser sealing is using a glass frit paste and screen printer. Laser sealing using glass frit paste has some problems, such as pores, nonuniform height, imperfect hermetic sealing, etc. In order to overcome these problems, sealing using fiber types of sealant is attractive for packaging devices. In this work, (70-x)V2O5-5ZnO-22BaO-3B2O3-xM(PO3)n glasses (mol%) incorporated with xM(PO3)n concentration (where M = Mg, Al, n = 2, 3, respectively) were fabricated and their thermal, thermomechanical, and structural properties were investigated. Most importantly, for this type of sealing, the glass should have a thermal stability (ΔT) of ≥80 °C and the coefficient of thermal expansion (CTE) between the glass and panel should be 1.0 ppm/°C. The highest thermal stability ΔT of the order of 93.2 °C and 112.9 °C was obtained for the 15 mol% of Mg(PO3)2 and Al(PO3)3 doped glasses, respectively. This reveals that the bond strength and connectivity is more strongly improved by trivalent Al(PO3)3. The CTE of a (70-x)V2O5-5ZnO-22BaO-3B2O3-xAl(PO3)3 glass system (mol%) (where x = 5–15, mol%) is in the range of 9.5–15.5 (×10−6/K), which is comparable with the CTE (9–10 (×10−6/K)) of commercial DSSC glass panels. Based on the results, the studied glass systems are considered to be suitable for laser sealing using fiber types of sealant.

A contribution to the exploration of the chemical durability, thermal stability, and structural ability of glasses from the Fe\(_{2}\)O\(_{3}\)-K\(_{2}\)O-MoO\(_{3}\)-P\(_{2}\)O\(_{5}\) quaternary system

“…Phosphate glass materials represent a great interest in technological fields. They are widely studied in research [2][3][4][5][6][7][8][9][10][11][12][13]. However, their relatively poor chemical durability limits their use.…”