Surface‐Modified TiO₂ Photocatalysts Prepared by a Photosynthetic Route: Mechanism, Enhancement, and Limits

Abstract

Surface‐modified TiO2 photocatalysts were synthesized by a photosynthetic route involving visible‐light‐induced (λ>455 nm) activation of benzene and toluene at the surface of TiO2 leading to the formation of carbonaceous polymeric deposits. IR spectroscopic and photoelectrochemical experiments showed that the mechanism of the photosynthetic reactions involves intra‐bandgap surface states at TiO2 related to surface OH groups interacting with adsorbed aromatic molecules. The photosynthesized surface‐modified TiO2 materials exhibited enhanced activity, relative to pristine TiO2, in photocatalytic degradation (and complete mineralization) of 4‐chlorophenol. The improvement was pronounced particularly under visible‐light (λ>455 nm) irradiation with the relative initial photodegradation rate enhanced by a factor of four. The surface‐modified photocatalysts exhibited good stability under the operating conditions, and the optimum carbon content was approximately 0.5 wt %. Mechanistic studies showed that the enhanced visible‐light photodegradation of 4‐chlorophenol is due to modified surface‐adsorption properties that facilitate formation of a surface complex between titania and 4‐chlorophenol, rather than due to any sensitizing effect of the carbonaceous deposits. The study highlights the importance of considering the interaction between pollutant molecules and the photocatalyst surface in heterogeneous photocatalysis, and possibly opens up a route for photosynthesis of further surface‐modified photocatalysts with tuned surface properties.

Synthesis of Phase Pure Hexagonal YFeO3 Perovskite as Efficient Visible Light Active Photocatalyst

“…Such excitation of adsorbed aromatic systems was, for example, reported by Neubert et al [49]. Superoxide radicals (·O 2 − ) would react further with water molecules to hydroxyl radicals.…”

Viologen‐Templated Arrays of Cucurbit[7]uril‐Modified Iron‐Oxide Nanoparticles

“…Strunk erhielt den Preis für ihre Arbeiten über die photokatalytische Reduktion von Kohlendioxid mit Wasser unter Bildung von Kohlenwasserstoffen. Sie hat in ChemPlusChem über TiO 2 ‐Photokatalysatoren berichtet2a und in ChemSusChem über Cokatalysatoren für die photokatalytische Wasserspaltung 2b…”

Applications of Mesoporous Ordered Semiconductor Materials — Case Study of TiO2

“…They reported that, in trials where they employed n-type TiO 2 as anode and Platinum as cathode, when TiO 2 electrode illuminated under short-circuit conditions, hydrogen evolved from the Platinum electrode, while oxygen evolved from the anode. Since then, studies aimed at discovering and exploring different possibilities of technological application for TiO 2 have been given great importance [14][15][16][17][18][19][20][21][22].…”

“…The photocatalytic efficiency of TiO 2 depends on its structural and morphological characteristics, which are related to the method of synthesis used in the preparation of nanoparticles [18,21,29,45]. To be photoactive, favoring the photocatalysis process, besides being mainly consisting of anatase crystalline phase, the TiO 2 must possess high specific surface area, good porosity, with high sized pores [35,45,46].…”