“…Also, at the highest ablation time, small particle sizes are obtained with high volume fractions in the chitosan solution than water. Additionally, the TEM images show very scattered, non-agglomerated Zn-NPs with spheroidal or near-spherical morph ology [27]. The 3D-graph (figure 6) indicates a clear relationship between particle size, ablation time and volume fraction of Zn-NPs in the chitosan solution.…”

Section: Characterizationmentioning

confidence: 94%

Improving stability of zinc nanoparticles in chitosan solution with a nanosecond pulsed laser

et al. 2019

View full text Add to dashboard Cite

A green method is presented to fabricate zinc nanoparticles using laser ablation synthesis in a natural polymer solution. The main aims are to reduce the zinc nanoparticles size and to increase their stability by using different ablation times in a chitosan solution as a natural polymer stabilizer. A Nd:YAG pulsed laser (532 nm) of energy 60 mJ/pulse, with a pulse duration of 10 ns was used to ablate a zinc plate immersed in chitosan solution from which the nanoparticles were produced. The average particle sizes as well as the volume fraction of the zinc nanoparticles in the solution were measured at 5, 10, 15, 30 min of ablation time. The results showed that the particle size decreased from 9.43 to 5.04 nm with spherical morphology and its volume fraction increased from 0.24 × 10−7 to 8.5 × 10−7 as the ablation time progressed from 5 to 30 min respectively. As a comparative study, a reasonable decrease was observed in the particle size for chitosan than distilled water. It was also noted that the stability and dispersion of zinc nanoparticles were much higher in the chitosan solution compared to water. In addition, the COSMO (conductor-like screening model) solvation model was used to compare the enthalpies of Zn-NPs in different media. Obtained results confirmed their stability was higher when merged in a natural polymer compared to water.

show abstract

Section: Characterizationmentioning

confidence: 94%