Synthesis and Optical Properties of Cobalt-Modified Titanium Oxide Films

Logacheva, V. A.; Лукин, А. Н.; Afonin, N. N.; Serbin, O. V.

doi:10.1134/s0030400x19060158

Cited by 3 publications

(1 citation statement)

References 37 publications

Supporting

Mentioning

Contrasting

Order By: Relevance

“…Oxide material-based Ti and Co are also prepared as thin-film coatings. They can have the form of single films [5,10,28,29] and multilayers [30][31][32] (Figure 3b). According to the literature, magnetron sputtering [10,[33][34][35], Metal Organic Chemical Vapor Deposition (MOCVD) [28], epitaxy [5], or sol-gel [7,36] are primarily used for their manufacture.…”

Section: Introductionmentioning

confidence: 99%

Influence of Co-Content on the Optical and Structural Properties of TiOx Thin Films Prepared by Gas Impulse Magnetron Sputtering

et al. 2023

View full text Add to dashboard Cite

Nonstoichiometric (Ti,Co)Ox coatings were prepared using gas-impulse magnetron sputtering (GIMS). The properties of coatings with 3 at.%, 19 at.%, 44 at.%, and 60 at.% Co content were compared to those of TiOx and CoOx films. Structural studies with the aid of GIXRD indicated the amorphous nature of (Ti,Co)Ox. The fine-columnar, homogeneous microstructure was observed on SEM images, where cracks were identified only for films with a high Co content. On the basis of XPS measurements, TiO2, CoO, and Co3O4 forms were found on their surface. Optical studies showed that these films were semi-transparent (T > 46%), and that the amount of cobalt in the film had a significant impact on the decrease in the transparency level. A shift in the absorption edge position (from 337 to 387 nm) and a decrease in their optical bandgap energy (from 3.02 eV to more than 2.60 eV) were observed. The hardness of the prepared films changed slightly (ca. 6.5 GPa), but only the CoOx film showed a slightly lower hardness value than the rest of the coatings (4.8 GPa). The described studies allowed partial classification of non-stoichiometric (Ti,Co)Ox thin-film materials according to their functionality.

show abstract