Synthesis, thermal treatment, and characterization of sintered hard magnetic Fe–30Cr–16Co alloy

Ustyukhin, A. S.; Ankudinov, A. B.; Zelensky, V. A.; Алымов, М. И.; Milyaev, I. M.; Vompe, T. A.

doi:10.1016/j.jallcom.2022.163754

Cited by 9 publications

(1 citation statement)

References 34 publications

Supporting

Mentioning

Contrasting

Order By: Relevance

“…It is worth noting that the method of mixing elemental powders, which is widely used in the fabrication of medium-entropy alloys, is not used for high-entropy alloys [28].…”

Section: Introductionmentioning

confidence: 99%

Fabrication, Microstructure, and Physico-Mechanical Properties of Fe–Cr–Ni–Mo–W High-Entropy Alloys from Elemental Powders

Ivannikov

Grebennikov

Klychevskikh

et al. 2022

Metals

View full text Add to dashboard Cite

In this work, 35Fe30Cr20Ni10Mo5W (wt.%) and 30Fe30Cr20Ni10Mo10W (wt.%) high-entropy alloys were fabricated using a powder metallurgy route. Powder mixtures for a hot-pressure process were obtained by the mixing and mechanical alloying of elemental powders. Mechanical alloying was carried out for 1, 2.5, 5, and 10 h. X-ray phase analysis of the powder mixtures showed that with increasing time of mechanical alloying, Face-Centered Cubic (FCC), Body-Centered Cubic (BCC), and nickel–iron intermetallic phases were formed in the structure, and the volume content of molybdenum and tungsten decreased. The hot-pressing was carried out at a pressure of 30 MPa and a temperature of 1200 °C for 30 min. The maximum densities of 8.14 ± 0.02 and 8.40 ± 0.01 g/cm3 and compressive strengths of 2430 ± 30 MPa and 2460 ± 35 MPa for consolidated materials were achieved using powder mixtures after 10 h of mechanical milling, for compositions with 5 wt.% W and 10 wt.% W, respectively. The workpieces fabricated with a pressure-assisted sintering process from milled powders were found to consist of FCC, BCC, and sigma phases.

show abstract

“…It is worth noting that the method of mixing elemental powders, which is widely used in the fabrication of medium-entropy alloys, is not used for high-entropy alloys [28].…”

Section: Introductionmentioning

confidence: 99%