The Annealing Kinetics of Defects in CVD Diamond Irradiated by Xe Ions
Eugene A. Kotomin,
Vladimir N. Kuzovkov,
Aleksandr Lushchik
et al.
Abstract:The radiation-induced optical absorption at 1.5–5.5 eV (up to the beginning of fundamental absorption) has been analyzed in CVD diamond disks exposed to 231-MeV 132Xe ions with four fluences from 1012 to 3.8 × 1013 cm−2. The 5 mm diameter samples (thickness 0.4 mm) were prepared by Diamond Materials, Freiburg (Germany); the average grain size at growth site was around 80 μm; and the range of xenon ions was R = 11.5 μm. The intensity of several bands grows with ion fluence, thus confirming the radiation-induced… Show more
Set email alert for when this publication receives citations?
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.