The change of steel surface chemistry regarding oxygen partial pressure and dew point

Norden, Martin; Blumenau, Marc; Wuttke, Thiemo; Peters, Klaus-Josef

doi:10.1016/j.apsusc.2012.12.103

Cited by 29 publications

(13 citation statements)

References 17 publications

Supporting

Mentioning

Contrasting

Unclassified

Order By: Relevance

“…Amostras dos materiais processados foram obtidas para a realização deanálises (metalográficas, MEV, EDS) para efeito de comparaçãocom processo inicial (T P )avaliando-se a morfologia e composição química tanto da camada intermetálica quanto a oxidação seletiva superficial quando presentes. As primeiras amostras analisadas foram para ponto de orvalho T P +15, em que se espera encontrar uma estrutura similar às apresentadas pelo grupo de Bellhouse e McDermid [6,7] que utiliza valores similares e mesmos teores de H2que possui influência significativa sobre o material [8,9]. Assim, a Figura 04apresenta a constituição uniforme e homogênea da camada intermetálica, na qual a morfologia observada nessa região corresponde ao formato típico de "grãos de arroz", característica da camada intermetálica Fe 2 Al 5 Zn x (Figura 04c), a qual propicia melhor a aderência entre o aço e o revestimento.…”

Section: Avaliação Da Alteração Do Ponto De Orvalhounclassified

“…Assim, a Figura 04apresenta a constituição uniforme e homogênea da camada intermetálica, na qual a morfologia observada nessa região corresponde ao formato típico de "grãos de arroz", característica da camada intermetálica Fe 2 Al 5 Zn x (Figura 04c), a qual propicia melhor a aderência entre o aço e o revestimento. A seção transversal da amostra, detalhada pela Figura 05, reforça a morfologia encontrada para a camada intermetálica que não corresponde às observadas em [8,9], até mesmo para ponto de orvalhomais negativo. Além disso, oEDS realizado na região de interface camada intermetálica/substrato indica a possível presença de oxidação intergranular, com composição química de O, Fe, Mn, Al e Si, em consonância com a literatura [10].…”

Section: Avaliação Da Alteração Do Ponto De Orvalhounclassified

See 1 more Smart Citation

Influência Do Ponto De Orvalho Na Oxidação Seletiva Dos Ahss

Farias¹,

Correia²,

Miranda³

et al. 2019

ABM Proceedings

View full text Add to dashboard Cite

Resumo A oxidação seletiva dos elementos de liga se apresenta como importante fator de influência na capacidade de galvanizar a quente os aços avançados de alta resistência (AHSS-Advanced High Strength Steel). Essa indesejável oxidação,quando na superfície do aço, reduz a molhabilidade do zinco, o que resulta em dificuldades de se obter aderência do revestimento e impossibilidade posterior de processamento e aplicação do material. Com o objetivo de avaliar as características da oxidação seletiva e o impacto da mesma na formação da camada intermetálica Fe2Al5Znx e consequente aderência do revestimento, foi processado o aço TRIP 1,5% Al numa linha de galvanização com aplicação de revestimento Extragal® (GI). Nestes testes industriais, foram utilizados diferentes valores de ponto de orvalho através da injeção de vapor de água numa atmosfera protetiva N 2 +H 2 .Neste processo,o modo como a oxidação seletiva ocorre é modificado, possibilitando a formação da camada intermetálica, bem como adesão do revestimento. Amostras dos testes foram avaliadas e caracterizadas utilizando as técnicas de microscopia óptica, MEV e EDS.

show abstract

Section: Avaliação Da Alteração Do Ponto De Orvalhounclassified

Influência Do Ponto De Orvalho Na Oxidação Seletiva Dos Ahss

Farias¹,

Correia²,

Miranda³

et al. 2019

ABM Proceedings

View full text Add to dashboard Cite

show abstract

“…In industry, this oxidation phenomenon is characteristic of AISI 430 and does not take place in austenitic or duplex stainless steels. According to literature [8][9][10], the diffusivity of oxygen and alloying elements is more favoured in ferritic than in austenitic or duplex stainless steels.…”

Section: Introductionmentioning

confidence: 99%

Characterisation of High Temperature Oxidation Phenomena during AISI 430 Stainless Steel Manufacturing under a Controlled H2 Atmosphere for Bright Annealing

García

Núñez

Bello

et al. 2021

Metals

View full text Add to dashboard Cite

Localised-in-the-edge oxidation of four AISI 430 alloys was investigated after an industrial bright annealing process. The oxidised surface of each specimen was characterised by X-ray photoelectron spectroscopy (XPS), Raman-spectroscopy and SEM. The results showed that the selective oxidation of Cr and Mn took place at the coil edges of AISI 430. This led to the formation of an oxide scale based on Cr2O3 and MnCr2O4. On the other hand, the formation of Cr(OH)3 and MnOOH in the outer part of the oxide scale was related to the effect of the H2–N2 environment on the annealing furnace. The results concluded that the composition of Cr and Mn in the alloy determined the composition of the oxidation products. However, the effect of annealing time was minor in this oxidation mechanism, which slightly contributed to an increase in the cation diffusion from the steel to the oxide. Finally, the results obtained indicate that the colouration of the coil edges displayed in each studied material varies according to the alloy chemical composition and annealing time.

show abstract

“…IF steel coated better than the DP steels and did not exhibit uncoated areas, which indicates that the poor coatability is due to the effect of the steel chemistry and not other galvannealing process conditions. In the current study, lab simulations were not done using high dew points 16) or preoxidation/ reduction 17) to improve the coatability of the steel. The aim was to evaluate change in galvannealing with increasing Mo in the steel.…”

Section: Visual Observationsmentioning

confidence: 99%

Influence of Substrate Molybdenum on Galvannealing Kinetics of an Advanced High Strength Steel

2014

View full text Add to dashboard Cite

Advanced high strength steels (AHSS) are used for car body applications in the automotive industry to improve passenger safety, improve fuel efficiency and to lower harmful carbon emissions. Galvannealed AHSS are used to provide corrosion protection. AHSS are alloyed with several elements such as Mn, Si, Al, P, Mo, etc. to achieve better mechanical properties. However, the knowledge of the effects of Mo on galvannealing behavior is limited. This investigation was conducted to study the influence of molybdenum in steel on galvannealing kinetics. Five dual-phase steels with Mo varying from 0 wt% to 0.4 wt% were used for this study. The results showed a delay in the galvannealing kinetics with an increase in the steel molybdenum content. No obvious improvement in the coating appearance was observed with increasing molybdenum.

show abstract

The change of steel surface chemistry regarding oxygen partial pressure and dew point

Cited by 29 publications

References 17 publications

Influência Do Ponto De Orvalho Na Oxidação Seletiva Dos Ahss

Influência Do Ponto De Orvalho Na Oxidação Seletiva Dos Ahss

Characterisation of High Temperature Oxidation Phenomena during AISI 430 Stainless Steel Manufacturing under a Controlled H2 Atmosphere for Bright Annealing

Influence of Substrate Molybdenum on Galvannealing Kinetics of an Advanced High Strength Steel

Contact Info

Product

Resources

About