The Effect of Ce Addition on Corrosion Behavior of Permanent Mold Casting Mg-4Al-2Sn-1Ca alloy

Abstract

In the present work, the effect of adding Ce on the corrosion behavior of Mg-4Al-2Sn-1Ca alloy was investigated. The studied alloys were fabricated by gravity casting method and a potentiodynamic polarization, A.C. impedance and hydrogen evolution tests were carried out in a 3.5% NaCl solution with pH 7.2 at room temperature to measure the corrosion properties of Mg-4Al-2Sn-1Ca-xCe alloys. The microstructure of the Mg-4Al-2Sn-1Ca alloy was composed of α-Mg, Mg17Al12, Mg2Sn and CaMgSn phase. Also, a Al 11 Ce 3 phase was newly formed by the addition of Ce. With an increase of the Ce contents, the microstructure became refined and the corrosion resistance improved.Key words: Permanent mold casting, Mg-4Al-2Sn-1Ca-xCe alloy, Corrosion properties.

Comparison of Electrochemical Corrosion Properties of Permanent Mold Casting GZ21 Alloy and AZ91 Alloy

“…Mg-Al-Ca, Mg-Al-RE계 합금이 있다 [11][12][13][14]. 하지만 마그네 슘 합금의 내식성을 향상시키는 방법에는 (1) α-Mg과 갈바닉 부식을 유발하는 Mg 17 Al 12 상을 억제하는 방법과 (2) Ca, Li 등의 원소를 첨가하여 Mg 부식과정에서 생성되는 Mg(OH) 2 피막을 안정화 시키는 방법 등이 보고 되고 있으나, 아직 많 은 연구가 필요한 실정이다 [6,11].…”

“…하지만 마그네 슘 합금의 내식성을 향상시키는 방법에는 (1) α-Mg과 갈바닉 부식을 유발하는 Mg 17 Al 12 상을 억제하는 방법과 (2) Ca, Li 등의 원소를 첨가하여 Mg 부식과정에서 생성되는 Mg(OH) 2 피막을 안정화 시키는 방법 등이 보고 되고 있으나, 아직 많 은 연구가 필요한 실정이다 [6,11]. 최근 수행된 Mg-xSn 이원계 합금의 부식 특성 분석에 관 한 결과는 결정립계에 형성된 Eutectic Mg/Mg 2 Sn 상의 계 면에서 부식이 우선적으로 진행됨으로써 합금의 내식성을 상 당히 향상시켰다 [7][8][9].…”