The Influence of Shielding Gases on Keyhole-Induced Porosity and Nitrogen Absorption in SS 304 Stainless Steel Fiber Laser Welds

Abstract

As regards porosity formation and gas content, choosing the appropriate shielding gas for laser welding is essential for achieving high-quality joints. Keyhole-induced porosity formation tendency and, nitrogen content in fiber laser SS 304 stainless steel welds were investigated based on shielding gas nitrogen contents in fiber laser welding. Beads-on-plate autogenous welds were made at 5 kW continuous wave (CW) fiber laser in N2 and Ar mixtures. Optical metallography, Micro-focused X-ray, X­ray radiography, and High-speed images of the molten pool were used to investigate the porosity formation. In addition, a gas analyzer was used to study the weld metal nitrogen content. The results show that nitrogen has a significant impact on the reduction of porosity in the melting zone, increases the dissolved nitrogen in the solidified weld metal, while almost no significant effect on the keyhole mode.

Dissimilarly Laser Welded High Entropy Alloy and Stainless Steel 304

“…The choice of laser welding parameters is rationalized based on an extensive review and prior studies, ensuring the optimization of power, speed, and focus for achieving sound weld joints. The role of shielding gases, particularly nitrogen, is highlighted, drawing from recent research demonstrating its effectiveness in mitigating porosity during laser welding by Hafez, 2022 [4].…”