The Investigation of Structure Heterogeneous Joint Welds in Pipelines

Abstract

Abstract. Welding joints of dissimilar steels don't withstand design life. One of the important causes of premature destructions can be the acceleration of steel structural degradation due to cyclic mechanical and thermal gradients. Two zones of tube from steel 12H18N9T, exhibiting the structural instability at early stages of the decomposition of a supersaturated solid austenite solution, were subjected to investigation. Methods of x-ray spectral and structure analysis, micro hardnessmetry were applied for the research. Made the following conclusions, inside and outside tube wall surfaces of hazardous zones in welding joint have different technological and resource characteristics. The microhardness very sensitive to changes of metal structure and can be regarded as integral characteristic of strength and ductility. The welding processes are responsible for the further fibering of tube wall structure, they impact to the characteristics of hot-resistance and long-term strength due to development of ring cracks in the welding joint of pipeline. The monitoring of microhardness and structural phase conversions can be used for control by changes of mechanical properties in result of post welding and reductive heat treatment of welding joints.

The microhardness and internal stresses allocation in superheating pipes welded node made of dissimilar steels

“…On the other hand, technological modes of pipes production predetermine the appearance of significant discontinuity that will cause a high level of internal structural stresses with reduced material resistance to fracture [3,4].…”