Thermal deformation strengthening of WC-10Co4Cr coating prepared by high velocity air-fule process

Abstract

In this paper, WC-10Co4Cr coating was prepared on the surface of LC9 aluminum alloy by high velocity air-fule (HVAF) process. And a thermal deformation method was developed to enhance the coating properties. Experimental results show that, during the process of thermal deformation, the increase of temperature and deformation amount could improve the microhardness of coating surface. With temperature of 480°C and deformation amount of 16% (0.8 mm), the microhardness reached the maximum value of 1349 HV0.3, which increased nearly 20% compared with that of specimen (1137 HV0.3) without compressive deformation. Besides, the strengthening effects of thermal deformation temperature and deformation amount on the bonding strength of coating were obvious. With deformation temperature of 450°C and deformation amount of 8% (4 mm), the bonding strength reached the maximum critical load of 188 N, which was 17.5% higher than that of initial state.