Transport Properties and Solvent Induced-Crystallization in PET and PET-Clay Nanocomposite Films

Abstract

Transport properties and solvent induced-crystallization phenomena (SINC) in poly(ethylene terephthalate) (PET) and PET clay nanocomposites (nano-PET), prepared by melt intercalation, with a clay content of 5 % w/w, have been investigated. Films were obtained by hot pressing and characterized before and after the sorption in several solvents: toluene, benzene and chlorobenzene. Results of nonisothermal crystallization dynamics showed that the cold crystallization temperature, and the percent of crystallinity of Nano-PET films are higher than those of pure PET. The sorption of all of the used solvents is accompanied by a large-scale structural rearrangement, with leads to the induced crystallization of the original amorphous state. That solvent induced crystallization caused an increasing of up to four times the percent of crystallinity.

Panorama da Pesquisa Acadêmica Brasileira em Nanocompósitos Polímero/Argila e Tendências para o Futuro

“…Outro polímero bastante estudado para o preparo de nanocompósitos é o poli(tereftalato de etileno) (PET) [82][83][84][85][86][87][88] , polímero largamente empregado na indústria de embalagens. Dentre os trabalhos publicados por Pessan e colaboradores [89][90][91] , pode-se citar uma pesquisa na qual se estuda a influência do tipo de argila (as organofílicas Viscogel, Inpaltone e montmorilonita sódica organomodificada com cloreto de dialquildimetilamônio) no preparo de nanocompósitos de PET por intercalação por fusão, através do uso de um reômetro de torque. As argilas montmorilonita organomodificada e Viscogel não foram úteis na formação de nanocompósito por serem altamente empacotadas, impedindo a entrada das cadeias poliméricas e demonstrando que não bastava existir compatibilidade entre argila e polímero e sim, a existência de espaço livre para inserção das cadeias.…”