Tribological Behaviour of Gradient TiAlSiN Superhard Coatings

Abstract

The present study addresses the influence of the gradient microstructure of nanocrystalline TiAlSiN coatings on their tribological behaviour. Cathodic arc deposition was applied to elaborate such coatings, with a total thickness of 3.5 μm, onto stainless steel substrates. Their microstructure has been characterised via Transmission Electron Microscopy (TEM) and X-ray Photoelectron Spectroscopy (XPS) and has been reported in detail previously. Since the main application of TiN-based coatings is the enhancement of the anti-wear resistance of metallic substrates, this work is focused on the tribological performance of gradient TiAlSiN coatings under dry sliding conditions. For this purpose, tests were carried out in a ball-on-disc apparatus, using an alumina ball as counterbody. The influence of the sliding velocity on the evolution of the friction coefficient and the wear lifetime of the gradient coatings has been evaluated in comparison to those of TiN coatings of the same thickness, tested under the same experimental conditions. It was found that the gradient microstructure results in an increase of the coatings’ mean lifetime by an average factor of three.