Use of eco-benign periwinkle shell particle for making composites and study their effect on the thermal and mechanical properties of novel HDPE composites

Abstract

In this investigation, the shell powder of Littorina littorea commonly called periwinkle was used as an eco-benign filler in High-Density Polyethylene (HDPE) to form periwinkle/HDPE composites (PHPC). Understanding the effect of different particle sizes of periwinkle shell powder (PSP) and optimizing their influence on PHPC is the main scope of work. Periwinkle shell (PS) particle sizes from <53 μm to 150 μm were chosen as reinforcement. The different PSP size like <53 μm, 53 μm, 75 μm, 90 μm, 105 μm and 150 μm chosen in this study were named as PHPCL53, PHPC53, PHPC75, PHPC90, PHPC105, and PHPC150 respectively. The composites were fabricated by incorporating 1 weight % of PSP into HDPE matrix using compression molding technique and then subjected to morphological, thermal, and mechanical characterizations. Morphology studies using scanning electron microscope (SEM) confirms 150 μm PSP had best dispersion whereas 75 μm PSP resulted with agglomeration. PSP had little influence on the thermal stability of HDPE except for PHPC150 which showed rise in degradation temperature when compared to the neat sample. Mechanical properties such as hardness, Young’s modulus, impact strength, and flexural modulus were enhanced by the addition of PSP. Whereas, a decrease was noted in elongation at break (%) and flexural strength of PHPC indicating the stiffening effect of filler on HDPE. In order to understand the particle size influence better, the extension evaluation method (EEM) was performed for all samples and PHPC150 was found to be the best performing among all particle sizes.