Utilization of coconut fiber waste as a filling material for list profile

Abstract

List profile is a mineral board product that is increasingly in demand by the wider public. One of the advantages of list profiles is that they are cheap, quick to obtain, resistant to attacks by wood-destroying organisms, and can be obtained in the form of attractive ornaments. From an economic perspective, list profile with rofing filler is more expensive. Coconut fiber can be used as a type of filler that has the same strength at a low price. This research aims to determine the type and level of gypsum adhesive, white cement, and their mixtures on the properties of the coconut fiber list profile. The research design used a completely randomized design with Tukey’s follow-up test. The factors used were the type of adhesive (gypsum, white cement, and a mixture of gypsum with white cement), and the amount of adhesive (600 g, 690 g, and 780 g). The parameters observed were water content, density, thickness expansion, and fracture toughness. The research results showed that the type of adhesive had a significant effect on water content and thickness development, the amount of adhesive had a significant effect on density and the adhesive type had a significant effect on water content, while the amount of adhesive had a significant effect on density and thickness development. The average value of water content is 15.90 - 18.85 %, density 0.67 - 0.92 g/cm3, thickness expansion 0.37 - 2.54 % and strength at fracture 3.88 - 35.90 kg/cm2.