Анизотропия деформации памяти формы в монокристалле сплава Ni-=SUB=-49-=/SUB=-Fe-=SUB=-18-=/SUB=-Ga-=SUB=-27-=/SUB=-Co-=SUB=-6-=/SUB=-

Abstract

Stress-strain behavior of a cubic-shaped Ni49Fe18Ga27Co6 shape memory single crystal uniaxially compressed in three directions perpendicular to its faces was studied. The crystallographic orientation of the sample was chosen so that the sample was deformed along two <110>А and one [001]А directions. A fundamentally different stress-strain behavior was observed for the deformations along <110>A and [001]A directions. At room temperature, irrespective of the magnitude of the phase strain, the crystal compressed in [001]A exhibited superelastic behavior i.e. the strain fully recovered after unloading. In contrast, deformation along <110>A directions to the strain levels above 4% induced a residual shape memory strain after the unloading. Strains measured along the directions perpendicular to the compression axis indicate an anomalous behavior of the Poisson's ratio.

Влияние режима старения в мартенситном состоянии под сжимающей нагрузкой на двусторонний эффект памяти формы в монокристаллах ферромагнитного сплава Ni-=SUB=-49-=/SUB=-Fe-=SUB=-18-=/SUB=-Ga-=SUB=-27-=/SUB=-Co-=SUB=-6-=/SUB=-

“…1, a представлены кривые напряжение−деформация (σ −ε) в процессе СМН. Показано, что при развитии МП под нагрузкой как при T SIM1 = 373 K, так и при T SIM2 = 423 K на кривых σ −ε наблюдаются сбросы напряжений, что характерно для развития B2 − L1 0 МП под нагрузкой [110] B2 -направления при образовании сдвойникованного варианта мартенсита (correspondent variant pair (CVP) starin) (ε CVP = 3.2%) и его последующего раздвойникования (detwinning strain) (ε detw = 3.0%) [11,12]. Экспериментально показано, что, во-первых, при СМН (режимы I и II) необратимая деформация в цикле не превышает 0.5%.…”