Кристаллическая структура и магнитные характеристики твердых растворов Mn-=SUB=-1-x-=/SUB=-Fe-=SUB=-x-=/SUB=-NiGe

Abstract

Substitutional solid solutions Mn1-xFexNiGe (0.05≤x≤1.00) were synthesized. The crystal structure in the temperature range of 20 - 300 K has been studied by X-ray and neutron diffraction. At T = 200 K, a phase transformation from a hexagonal structure of the Ni2In type to an orthorhombic structure (S.G. Pnma) has been observed. The magnetic properties of these compounds were also investigated in the temperature range of 5 - 300 K and external magnetic fields up to 10 T. The temperature of the "magnetic order - magnetic disorder" phase transformation was found to decrease from 272 to 132 K with an increase in concentration x from 5 to 30 mol%.

Магнитоструктурные особенности фазовых переходов в системе Mn-=SUB=-1-x-=/SUB=-Co-=SUB=-x-=/SUB=-NiGe Часть 1. Экспериментальные результаты

“…Практический интерес к прямому (ПМКЭ) и обратному (ОМКЭ) магнитокалорическим эффектам [1][2][3][4], как правило, сопутствующим магнитным фазовым переходам порядок−беспорядок и порядок−порядок, соответственно, определяет актуальность исследования четырехкомпонентных сплавов типа Mn 1−x Cr x NiGe [5], MnNiGe 1−x Al x [6], MnNi 1−x Fe x Ge [7-9], Mn 1.9−x Ni x Ge [10], Mn 1−x Fe x NiGe [11][12], MnNi 1−x Co x Ge [13,14], MnCo 1−x Cu x Ge [15]. В данных системах наблюдается структурный фазовый переход типа смещения P6 3 /mmc(hex) ↔ P nma (orth) [16,17] и ряд магнитных фазовых переходов.…”