Composites including silicide of tungsten and boride of tungsten intermetallic compound as reinforced agents in alumina matrix have a good mechanical properties in low and high temperature (high friction resistance, strength, resin stance to creep and relatively high thermal shock resistance), moreover, they have chemical neutral with a high corrosion resistance in a high corrosive and high temperature environment. The purpose of this study is to investigate thermal analysis, phase and microstructural evaluation during synthesis of above mentioned composite by combustion aluminothermic processing in three systems 1-Al+Si+WO 3 , 2-Al+B 2 O 3 +WO 3 and 3-Al+B 2 O 3 +Si+WO 3. A Ball-milled starting material according to stoichiometric ratio was thermal analyzed (DTA-TGA) for each of above mentioned system. The XRD results never show any new phase during ball-milling even up to 10 hours. The forming of tungsten silicide (W x Si y) is in lower temperature in comparison with tungsten boride (W x B y) during the thermal analysis experiments. The presence of Si in the Al+B 2 O 3 +WO 3 system facilitates the formation of tungsten borides. The microstructural observations show a uniform and dense distribution of silicide and boride of tungsten in the alumina matrix. Silicide phases are small grain with spherical morphology whereas; the boride phases are coarser and relatively elongated with irregular morphology.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.