Tin sulfide (Snx Sy) thin films were prepared by a spray ultrasonic technique on glass substrate at 300 °C. The influence of deposition time t = 2, 4, 6, 8 and 10 min on different properties of thin films, such as (XRD), photoluminescence (PL) and (UV) spectroscopy visible spectrum and four-point were investigated. X-ray diffraction showed that thin films crystallized in SnS2, SnS, and Sn2S3 phases, but the most prominent one is SnS2. The results of the (UV) spectroscopy visible spectrum show that the film which was deposited at 4 min has a large transmittance of 60% in the visible region. The photoluminescence spectra exhibited the luminescent peaks in the visible region, which shows its potential application in photovoltaic devices. The electrical resistivity (ρ) values of SnxSy films have changed from 8.1 × 10−4 to 1.62 Ω·cm with deposition time.
The aim of this work is to investigate the dependence of ZnS thin films structural and optical properties with the solution flow rate during the deposition using an ultrasonic spray method. The solution flow rate ranged from 10 to 50 mL/h and the substrate temperature was maintained at 450 °C. The effect of the solution flow rate on the properties of ZnS thin films was investigated by X-ray diffraction (XRD), scanning electron microscopy (SEM), optical transmittance spectroscopy (UV–V) and the four-point method. The X-ray diffraction analysis showed that the deposited material was pure zinc sulphide, it has a cubic sphalerite structure with preferential orientation along the (111) direction. The grain size values were calculated and found to be between 38 to 82 nm. SEM analysis revealed that the deposited thin films have good adherence to the substrate surfaces, are homogeneous and have high density. The average transmission of all films is up more than 65% in the range wavelength from 200 to 1100 nm and their band gap energy values were found between 3.5–3.92 eV. The obtained film thickness varies from 390 to 1040 nm. Moreover, the electric resistivity of the deposited films increases with the increasing of the solution flow rate between 3.51 × 105 and 11 × 105 Ω·cm.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.