No abstract

In this study, a Pt/anodized aluminum oxide (AAO) catalyst was prepared by the anodization of an Al alloy (Al6082, 97.5% Al), followed by the incorporation of Pt via an incipient wet impregnation method. Then, the Pt/AAO catalyst was evaluated for autocatalytic hydrogen recombination. The Pt/AAO catalyst’s morphological characteristics were determined by scanning electron microscopy (SEM) and transmission electron microscopy (TEM). The average Pt particle size was determined to be 3.0 ± 0.6 nm. This Pt/AAO catalyst was tested for the combustion of lean hydrogen (0.5–4 vol% H2 in the air) in a recombiner section testing station. The thermal distribution throughout the catalytic surface was investigated at 3 vol% hydrogen (H2) using an infrared camera. The Al/AAO system had a high thermal conductivity, which prevents the formation of hotspots (areas where localized surface temperature is higher than an average temperature across the entire catalyst surface). In turn, the Pt stability was enhanced during catalytic hydrogen combustion (CHC). A temperature gradient over 70 mm of the Pt/AAO catalyst was 23 °C and 42 °C for catalysts with uniform and nonuniform (worst-case scenario) Pt distributions. The commercial computational fluid dynamics (CFD) code STAR-CCM+ was used to compare the experimentally observed and numerically simulated thermal distribution of the Pt/AAO catalyst. The effect of the initial H2 volume fraction on the combustion temperature and conversion of H2 was investigated. The activation energy for CHC on the Pt/AAO catalyst was 19.2 kJ/mol. Prolonged CHC was performed to assess the durability (reactive metal stability and catalytic activity) of the Pt/AAO catalyst. A stable combustion temperature of 162.8 ± 8.0 °C was maintained over 530 h of CHC. To confirm that Pt aggregation was avoided, the Pt particle size and distribution were determined by TEM before and after prolonged CHC.

Spatial heating and cooking account for a significant fraction of global domestic energy consumption. It is therefore likely that hydrogen combustion will form part of a hydrogen-based energy economy. Catalytic hydrogen combustion (CHC) is considered a promising technology for this purpose. CHC is an exothermic reaction, with water as the only by-product. Compared to direct flame-based hydrogen combustion, CHC is relatively safe as it foregoes COx, CH4, and under certain conditions NOx formation. More so, the risk of blow-off (flame extinguished due to the high fuel flow speed required for H2 combustion) is adverted. CHC is, however, perplexed by the occurrence of hotspots, which are defined as areas where the localized surface temperature is higher than the average surface temperature over the catalyst surface. Hotspots may result in hydrogen’s autoignition and accelerated catalyst degradation. In this review, catalyst materials along with the hydrogen technologies investigated for CHC applications were discussed. We showed that although significant research has been dedicated to CHC, relatively limited commercial applications have been identified up to date. We further showed the effect of catalyst support selection on the performance and durability of CHC catalysts, as well as a holistic summary of existing catalysts used for various CHC applications and catalytic burners. Lastly, the relevance of CHC applications for safety purposes was demonstrated.

No abstract

No abstract