The BaCe 0.7 Zr 0.1 Y 0.2-x Zn x O 3- (x = 0.05, 0.10, 0.15, 0.20) has been synthesized by the conventional solid state reaction method for application in protonic solid oxide fuel cell. The phase purity and lattice parameters of the materials have been studied by the room temperature X-ray diffraction (XRD). Scanning electron microscopy (SEM) has been done for check the morphology and grain growth of the samples. The chemical and mechanical stabilities have been done using thermogravimetric analysis (TGA) in pure CO 2 environment and thermomechanical analysis (TMA) in Argon atmosphere. The XRD of the materials show the orthorhombic crystal symmetry with Pbnm space group. The SEM images of the pellets show that the samples sintered at 1200 o C are highly dense. The XRD after TGA in CO 2 and thermal expansion measurements confirm the stability. The particles of the samples are in micrometer ranges and increasing Zn content decreases the size. The conductivity measurements have been done in 5% H 2 with Ar in dry and wet atmospheres. All the materials show high proton conductivity in the intermediate temperature range (400-700 o C). The maximum proton conductivity was found to be 1.0 10-2 S cm-1 at 700 o C in wet atmosphere for x = 0.10. From our study, 10 wt % of Zn seems to be optimum at the B-site of the perovskite structure. All the properties studied here suggest it can be a promising candidate of electrolyte for IT-SOFCs.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.