This paper presents the wear characteristics of the composite ceramic coating made with Al2O3-40wt%8YSZ on the biomedical grade Ti-6Al-4V alloy (grade 5) used for total joint prosthetic components, with the aim of improving their tribological behavior. The coatings were deposited using a plasma spraying technique, and optimization of plasma parameters was performed using response surface methodology to obtain dense coating. The tribological behaviors of the coated and uncoated substrates were evaluated using a ball-on-plate sliding wear tester at 37°C in simulated body-fluid conditions. The microstructure of both the titanium alloy and coated specimen were examined using an optical microscope and scanning electron microscope. The hardness of the plasma-sprayed alumina–zirconia composite coatings was 2.5 times higher than that of the Ti-6Al-4V alloy, while the wear rate of Ti-6Al-4V alloy was 253 times higher than that of the composite-coated Ti-6Al-4V alloy. The superior wear resistance of the alumina–zirconia coated alloy is attributed to its enhanced hardness and intersplat bonding strength. Wear-track examination showed that the predominant wear mechanism of Ti-6Al-4V alloy was abrasive and adhesive wear, whereas, in the case of alumina–zirconia composite coated alloy, the wear was dominated by microchipping and microcracking.
In this research, boron carbide (B4C) and titanium carbide (TiC) nanoparticles were deposited along with Nickel on AZ80 magnesium alloy substrates. Triangular waveform pulse current was used for depositing the coatings on the substrate. The objective of this research is to investigate the microstructural evolution of the coatings in response to the current density, duty cycle and the concentration of reinforcements in the bath. The influence of process parameters were also assessed in terms of the microhardness and specific wear rate. To enhance the surface properties of AZ80 magnesium alloy, a three component layer was successfully applied via electro co-deposition technique for the first time. The magnesium alloy substrates were cleaned and pretreated as per ASTM B480−88. The pretreated samples were coated at three levels of current density viz. 1.5 A/dm2, 2 A/dm2 and 2.5 A/dm2, and the duty cycle was varied between 30%, 40% and 50%. The concentrations of reinforcements in the bath were kept at 0 g/L, 0.5 g/L and 1 g/L. The samples were coated according to Taguchi L9 orthogonal array with two replications. The microstructural studies conducted using scanning electron microscope (SEM) revealed the defects, grain refinement and homogeneous distribution of reinforcements in the Ni matrix. The deposition and orientation of reinforcements in preferred planes were investigated with XRD. Vickers microhardness tests conducted as per ASTM E384-17 revealed that the sample coated with 2.5 A/dm2current density, 30 % duty cycle, 1 g/L B4C and 0.5 g/L TiC produced the coatings with the highest hardness of 412.56 Hv. The results of the pin on disc wear tests conducted according to ASTM G99 were in agreement with the hardness results and the corresponding microstructure. The sample with the maximum microhardness exhibited the minimum specific wear rate of 2.1 E-08 mm3/Nm. The ability of triangular pulse current waveform to deposit hybrid composite coatings on AZ80 magnesium alloy and enhance its surface properties has been confirmed by the results of this research.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.