Heavily boron doped diamond epilayers with thicknesses ranging from 40 to less than 2 nm and buried between nominally undoped thicker layers have been grown in two different reactors. Two types of [100]-oriented single crystal diamond substrates were used after being characterized by X-ray white beam topography. The chemical composition and thickness of these so-called delta-doped structures have been studied by secondary ion mass spectrometry, transmission electron microscopy, and spectroscopic ellipsometry. Temperature-dependent Hall effect and four probe resistivity measurements have been performed on mesa-patterned Hall bars. The temperature dependence of the hole sheet carrier density and mobility has been investigated over a broad temperature range (6 K < T < 450 K). Depending on the sample, metallic or non-metallic behavior was observed. A hopping conduction mechanism with an anomalous hopping exponent was detected in the non-metallic samples. All metallic delta-doped layers exhibited the same mobility value, around 3.6 ± 0.8 cm2/Vs, independently of the layer thickness and the substrate type. Comparison with previously published data and theoretical calculations showed that scattering by ionized impurities explained only partially this low common value. None of the delta-layers showed any sign of confinement-induced mobility enhancement, even for thicknesses lower than 2 nm

Deep-ultraviolet (DUV) solar-blind photodetectors based on high-quality cubic boron nitride (cBN) films with a metal/semiconductor/metal configuration were fabricated. The design of interdigitated circular electrodes enables high homogeneity of electric field between pads. The DUV photodetectors present a peak responsivity at 180nm with a very sharp cutoff wavelength at 193nm and a visible rejection ratio (180 versus 250nm) of more than four orders of magnitude. The characteristics of the photodetectors present extremely low dark current, high breakdown voltage, and high responsivity, suggesting that cBN films are very promising for DUV sensing.