The paper presents results of the study of the effect of doping with yttrium oxide on ceramics of the composition (γ + θ) Al2O3 + nY2O3 (n = 0, 1, 2, 3 wt%), sintered at 1550°C for 2 h, from powders of the specified composition annealed at temperatures of 500 , 800, 1000°С. X-ray diffraction analysis established the formation in ceramics of yttrium aluminum garnet Y3Al5O12 (YAG) and a metastable phase of the same composition with a tetragonal lattice type in powders at temperatures above 1200°C. The effect of YAG on the physical and mechanical properties was established: high properties were demonstrated by ceramics of the composition α-Al2O3 + 2wt% Y2O3, obtained from a powder annealed at 1000°C. In addition, high physical and mechanical properties were observed in ceramics of the composition α-Al2O3 + 0wt% Y2O3, obtained from a powder annealed at 800°C. The effect of the so-called “mutual protection against crystallization” was discovered, which consists in the mutual inhibition of crystallization processes in powders of the Al2O3 – Y2O3 system.