The imaging properties and observation of the sterically regulated translational motion of discrete tungsten polyoxometalate Linqvist ions (i.e., [W(6)O(19)](2-)) within carbon nanotubes of specific internal diameter are reported. The translational motion of the nonspheroidal anion within the nanotube capillary is found to be impeded by its near-perfect accommodation to the internal van der Waals surface of the nanotube wall. Rotational motion of the anion about one remaining degree of freedom permits translational motion of the anion along the nanotube followed by locking in at sterically favorable positions in a mechanism similar to a molecular ratchet. This steric locking permits the successful direct imaging of the constituent octahedral cation template of individual [W(6)O(19)](2-) anions by high resolution transmission electron microscopy thereby permitting meterological measurements to be performed directly on the anion. Direct imaging of pairs of equatorial W(2) atoms within the anion reveal steric relaxation of the anion contained within the nanotube capillary relative to the bulk anion structure.
High functional ophthalmic lens materials, poly(HEMA-co-MMA)s were prepared by the copolymerization of HEMA, MMA, MA, EDGMA, and N,N-dimethylacrylamide in the presence of platinum nanoparticles with antimicrobial properties. The hydrophilic monomer N,N-dimethylacrylamide has excellent biocompatibility and oxygen transmissibility. The combination where platinum nanoparticles were added produced a colorless transparent lens. The water contents were in the range of 36.68-44.08% and the refractive index was measured to be in the range of 1.424-1.436. Meanwhile, the oxygen transmissibility ranged from 11.13 x 10(-11) to 17.63 x 10(-11) (cm2/sec) (mlO2/ml x mm Hg) increased with increasing the addition ratio of N,N-dimethylacrylamide. The physical properties measurements of the produced polymers showed that the nanoparticles did not show significant effect on the water content and refractive index of the hydrogel contact lens, but the materials effected to reduce oxygen permeability to a certain extent. The copolymers have excellent oxygen permeability, indicating that the material can be used to fabricate hydrogel contact lenses with high oxygen transmissibility.
ZnO nanoparticles and vinyl pyridine were added to the mixture of MMA (methyl methacrylate), HEMA (2-hydroxy ethyl methacrylate) and NVP (N-vinylpyrrolidone) in a mould at various concentrations. Cross-linker EGDMA (ethyleneglycoldimethacrylate) and AIBN (azobisisobutyronitrile) initiator were finally added to the mixture and then heated at 80 o C for 60 min to prepare high-performance hydrogel ophthalmic lens. The physical properties of the hydrogel ophthalmic material were investigated by measuring the average value of refractive index, water content and optical transmittance. The refractive index of 1.429~1.450, water content of 34~41%, and visible transmittance of 78~90% were obtained. The material is possibly used to manufacture UV-block hydrogel contact lens.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.