The present paper investigates the effects of simultaneous mechanical foaming using water and fluxing with a bio-derived agent on the properties of three distinct asphalt binders: 50/70 paving-grade bitumen, 45/80–55 polymer-modified bitumen, and 45/80–80 highly modified asphalt binder. The testing involved classical tests for assessing binder consistency (penetration at 25 °C, ring and ball softening point, Fraass breaking point, and dynamic viscosity) as well as performance tests (high and low Superpave critical temperatures and multiple stress creep recovery). The tests included assessment directly after asphalt binder foaming and were repeated after a 14-day period. It was shown that bitumen foaming had only short-term effects on the asphalt binders, which did not persist in the repeated tests after 14 days. The fluxing agent that was utilized caused significant changes in the consistency of all asphalt binders. The changes in the performance characteristics of the 50/70 and 45/80–55 binders were severe and amounted to a significant decrease in high-temperature performance of these binders. On the other hand, an improvement in all performance characteristics in the case of the 45/80–80 asphalt binder was observed as a result of the applied processes, particularly when measured 14 days after foaming. This study shows that the simultaneous use of foaming and the fluxing additive decreased the dynamic viscosity of the 45/80–80 binder, while improving its properties relating the pavement performance.

The present paper investigates the viscoelastic stress-strain responses of laboratory and plant produced warm mix asphalt mixtures containing basalt fiber dispersed reinforcement. The investigated processes and mixture components were evaluated for their efficacy in producing highly performing asphalt mixtures with decreased mixing and compaction temperatures. Surface course asphalt concrete (AC-S 11 mm) and high modulus asphalt concrete (HMAC 22 mm) conventionally and using a warm mix asphalt technique with foamed bitumen and a bio-derived fluxing additive. The warm mixtures included lowered production temperature (by 10 °C) and lowered compaction temperatures (by 15 °C and 30 °C). The complex stiffness moduli of the mixtures were assessed under cyclic loading tests at combinations of four temperatures and five loading frequencies. It was found that the warm produced mixtures were characterized by lower dynamic moduli than the reference mixtures in the whole spectrum of loading conditions, however, the mixtures compacted at the 30 °C lower temperature performed better than the mixtures compacted at 15 °C lower temperature, specifically when highest testing temperatures are considered. The differences in the performance of plant and laboratory produced mixtures were ascertained to be nonsignificant. It was concluded that the differences in stiffness of hot mix and warm mixtures can be attributed to the inherent properties of foamed bitumen mixtures and that these differences should shrink in time.