The preparation of chemically reduced graphene oxide (rGO) and the optimization of epoxy resins’ properties using micro or nanofillers are now common practices. rGO nanoparticles (60 nm) based on an epoxy resin polymer were prepared at the concentrations of 0, 1, 2, 3, 4, and 5% weight percentage with fixed 6-mm thicknesses. The dielectric properties of the composites were measured by the reflection/transmission technique in connection with a vector network analyser (VNA) at a frequency range of 8–12 GHz. The microwave absorption and shielding effectiveness properties were calculated by using the reflection S11 and transmission S21 results. The microstructure and morphology of the polymer and the rGO/cured epoxy composites were studied by field emission scanning electron microscopy (FE-SEM), Fourier-transform infrared (FT-IR) spectroscopy, and the X-ray Diffraction (X-RD) technique for characterizing crystalline materials. The dielectric and other properties of the rGO/cured epoxy composites were investigated based on the filler load and frequency. It was found that the applied frequency and the filler concentrations affected the dielectric properties of the rGO/cured epoxy composites. The results showed that the introduction of rGO particles to the composites increased their dielectric properties smoothly. The study of the dependence on frequency of both the dielectric constant ε′ and the dielectric loss ε″ showed a decrease in both quantities with increasing frequency, indicating a normal behaviour of the dielectrics. Cole–Cole plots were drawn with ε′ and ε″. A theoretical simulation in terms of the Cole–Cole dispersion law indicates that the Debye relaxation processes in the rGO/cured epoxy composites are improved due to the presence of the rGO filler. Moreover, with the addition of rGO as a filler into the Epoxy matrix, it now exhibits promise as a lightweight material for microwave absorption as well as an effective electromagnetic interference (EMI) shielding material.

The purpose of this study was to synthesize high-quality recycled α-Fe2O3 to improve its complex permittivity properties by reducing the particles to nanosize through high energy ball milling. Complex permittivity and permeability characterizations of the particles were performed using open-ended coaxial and rectangular waveguide techniques and a vector network analyzer. The attenuation characteristics of the particles were analyzed with finite element method (FEM) simulations of the transmission coefficients and electric field distributions using microstrip model geometry. All measurements and simulations were conducted in the 8–12 GHz range. The average nanoparticle sizes obtained after 8, 10 and 12 h of milling were 21.5, 18, and 16.2 nm, respectively, from an initial particle size of 1.73 µm. The real and imaginary parts of permittivity increased with reduced particle size and reached maximum values of 12.111 and 0.467 at 8 GHz, from initial values of 7.617 and 0.175, respectively, when the particle sizes were reduced from 1.73 µm to 16.2 nm. Complex permeability increased with reduced particle size while the enhanced absorption properties exhibited by the nanoparticles in the simulations confirmed their ability to attenuate microwaves in the X-band frequency range.

The development of microwave absorbing materials based on recycled hematite (α-Fe 2 O 3 ) nanoparticles and polycaprolactone (PCL) was the main focus of this study. α-Fe 2 O 3 was recycled from mill scale and reduced to nanoparticles through high energy ball milling in order to improve its complex permittivity properties. Different compositions (5% wt., 10% wt., 15% wt. and 20% wt.) of the recycled α-Fe 2 O 3 nanoparticles were melt-blended with PCL using a twin screw extruder to fabricate recycled α-Fe 2 O 3 /PCL nanocomposites. The samples were characterized for their microstructural properties through X - ray diffraction (XRD) and high resolution transmission electron microscopy (HRTEM). The complex permittivity and microwave absorption properties were respectively measured using the open ended coaxial (OEC) probe and a microstrip in connection with a vector network analyzer in the 1–4 GHz frequency range. An average α-Fe 2 O 3 nanoparticle size of 16.2 nm was obtained with a maximum imaginary (ε " ) part of permittivity value of 0.54 at 4 GHz. The complex permittivity and power loss values of the nanocomposites increased with recycled α-Fe 2 O 3 nanofiller content. At 2.4 GHz, the power loss (dB) values obtained for all the nanocomposites were between 13.3 dB and 14.4 dB and at 3.4 GHz, a maximum value of 16.37 dB was achieved for the 20 % wt. nanocomposite. The recycled α-Fe 2 O 3 /PCL nanocomposites have the potential for use in noise reduction applications in the 1–4 GHz range.

The purpose of this study was to improve the dielectric, magnetic, and thermal properties of polytetrafluoroethylene (PTFE) composites using recycled Fe2O3 (rFe2O3) nanofiller. Hematite (Fe2O3) was recycled from mill scale waste and the particle size was reduced to 11.3 nm after 6 h of high-energy ball milling. Different compositions (5–25 wt %) of rFe2O3 nanoparticles were incorporated as a filler in the PTFE matrix through a hydraulic pressing and sintering method in order to fabricate rFe2O3–PTFE nanocomposites. The microstructure properties of rFe2O3 nanoparticles and the nanocomposites were characterized through X-ray diffraction (XRD), field emission scanning electron microscopy (FESEM), and high-resolution transmission electron microscopy (HRTEM). The thermal expansion coefficients (CTEs) of the PTFE matrix and nanocomposites were determined using a dilatometer apparatus. The complex permittivity and permeability were measured using rectangular waveguide connected to vector network analyzer (VNA) in the frequency range 8.2–12.4 GHz. The CTE of PTFE matrix decreased from 65.28×10−6/°C to 39.84×10−6/°C when the filler loading increased to 25 wt %. The real (ε′) and imaginary (ε″) parts of permittivity increased with the rFe2O3 loading and reached maximum values of 3.1 and 0.23 at 8 GHz when the filler loading was increased from 5 to 25 wt %. A maximum complex permeability of 1.1−j0.07 was also achieved by 25 wt % nanocomposite at 10 GHz.

Epoxy resin (ER) composites reinforced with micro‐sized oil palm empty fruit bunch (OPEFB) were fabricated to improve the biodegradability of electromagnetic interference connector gasket. The dielectric properties, transmission coefficient |S21|, reflection coefficient |S11|, reflection loss, power loss and shielding effectiveness were studied at a frequency range of 8–12 GHz. OPEFB–ER composites were prepared by varying the percentages of OPEFB (0, 5, 10, 15, 20, 25, 30 and 40%) at room temperature (25°C ±2). Dielectric constant (ɛ′), loss factor (ɛ″), reflection and transmission coefficients of the composites were measured using rectangular waveguide connected to vector network analyser. In addition, ɛ′ and ɛ″ were used in finite element method technique to obtain |S11| and |S21|. The results showed that the dielectric properties increased but |S11| and |S21| decreased with increasing OPEFB percentage in the composites. The shielding effectiveness, power loss and reflection loss increased with increasing OPEFB percentage in the composites. The simulated and measured results of |S11| and |S21| were in good agreement.