Metal matrix syntactic foams (MMSFs) are advanced lightweight materials constituted by a metallic matrix and a dispersion of hollow/porous fillers. Physical and mechanical properties can be fitted regarding matrix and filler properties and processing parameters. Their properties make them potential materials for sectors where density is a limiting parameter, such as transport, marine, defense, aerospace, and engineering applications. MMSFs are mainly manufactured by powder metallurgy, infiltration, and stir casting techniques. This study focuses on the current stir casting approaches and on the advances and deficiencies, providing processing parameters and comparative analyses on porosity and mechanical properties. PRISMA approaches were followed to favor traceability and reproducibility of the study. Stir casting techniques are low-cost, industrially scalable approaches, but they exhibit critical limitations: buoyancy of fillers, corrosion of processing equipment, premature solidification of molten metal during mixing, cracking of fillers, heterogeneous distribution, and limited incorporation of fillers. Six different approaches were identified; four focus on limiting buoyancy, cracking, heterogeneous distribution of fillers, and excessive oxidation of sensitive matrix alloys to oxygen. These improvements favor reaching the maximum porosity of 54%, increasing the fillers’ size from a few microns to 4–5 mm, reducing residual porosity by ±4%, synthesizing bimodal MMSFs, and reaching maximum incorporation of 74 vol%.

Metal matrix syntactic foams (MMSF) are advanced cellular materials constituted by a system of a minimum of two phases, in which a dispersion of hollow particles is embedded by a continuous metal matrix. The incorporation of porous fillers favors the development of low-density materials with exceptional behavior for damping vibrations, impacts, and blast effects, shielding acoustic, thermal, and electromagnetic energies. There are three main techniques to produce them: infiltration casting technique (ICT), stir casting technique (SCT), and powder metallurgy technique (P/M). The first two techniques are used for embedding filler into lower melting point metallic matrices than fillers, in contrast to P/M. The present study demonstrates the feasibility of producing MMSF with components of similar melting points by ICT. The fillers were synthesized in-situ with aluminum and a natural foaming agent from wastes of Spanish white marble quarries. These novel aluminum syntactic foams (ASF) were mechanically characterized following the ISO-13314 and exhibited a porosity, plateau stress, and energy absorption capacity of 41%, 37.65 MPa, 8.62 MJ/m3 (at 35% of densification), respectively. These properties are slightly superior to equal porosity LECA ASF, making these novel ASF suitable for the same applications as LECA-ASF.