An experiment was conducted in the MIT Research Reactor (MITR) to irradiate triplex silicon carbide fuel cladding tubes under typical Pressurized Water Reactor conditions. Measurements were made to determine the impact of exposure on strength and swelling. The SiC clad tubes were fabricated by Ceramic Tubular Products (CTP) with dimensions typical of 15 x 15 commercial PWR reactor fuel. The triplex tubes contain 3 layers, an inner monolithic SiC layer to maintain hermeticity, a central SiC/SiC composite layer to provide a graceful failure mode in the event of an accident, and an outer SiC environmental barrier layer.Clad tubes were exposed to 300 o C pressurized water containing boric acid, lithium hydroxide, and hydrogen overpressure, typical of PWRs. Thirty nine (39) specimens of various types were exposed to coolant, some within the neutron flux region and some outside the neutron flux region. Twenty seven (27) were removed for examination and test after 4 months exposure. Following examination, twenty specimens were reinserted for additional exposure, along with 19 new specimens. The 4 month specimens were weighed and measured at MIT, and some were shipped to Oak Ridge National Laboratory (ORNL) where they were mechanically tested for hoop strength using a polyurethane plug test apparatus. Results were compared with the preirradiation strength and dimensions. Some specimens retained their original strength after exposure, others with a less homogeneous monolith, lost strength.

No abstract

No abstract

No abstract

No abstract