An anode material incorporating a sulfide is reported. SnS nanoparticles anchored onto reduced graphene oxide are produced via a chemical route and demonstrate an impressive capacity of 350 mA h g, exceeding the capacity of graphite. These results open the door for a new class of high capacity anode materials (based on sulfide chemistry) for potassium-ion batteries.
We describe a method for conformal coating of reduced graphene oxide (rGO) by stibnite nanocrystallites. First, graphene oxide (GO) supported amorphous hydroperoxoantimonate was produced using the recently introduced hydrogen peroxide synthesis route. Sulfurization of the amorphous antimonate yielded supported antimony(V) oxide nanoparticles and sulfur, which were then converted by high temperature vacuum treatment to 15−20 nm rGO supported stibnite. The usefulness of the new material and synthesis approach are demonstrated by highly efficient and stable lithium battery anodes. Since both sulfur lithiation and antimony−lithium alloying are reversible, they both contribute to the charge capacity, which exceeded 720 mA h g −1 after 50 cycles at a current density of 250 mA g −1 . The very small crystallite size of the stibnite provides a minimum diffusion pathway and allows for excellent capacity retention at a high rate (>480 mA h g −1 at 2000 mA g −1 was observed). The nanoscale dimensions of the crystallites minimize lithiation-induced deformations and the associated capacity fading upon repeated charge−discharge cycles. The flexibility and conductivity of the rGO ensure minimal ohmic drop and prevent crack formation upon repeated cycles.
A highly stable sodium ion battery anode was prepared by deposition of hydroperoxostannate on graphene oxide from hydrogen-peroxide-rich solution followed by sulfidization and 300 C heat treatment. The material was characterized by electron microscopy, powder X-ray diffraction and X-ray photoelectron spectroscopy which showed that the active material is mostly rhombohedral SnS 2 whose (001) planes were preferentially oriented in parallel to the graphene oxide sheets. The material exhibited >610 mA h g À1 charge capacity at 50 mA g À1 (with >99.6% charging efficiency) between 0 and 2 V vs. Na/Na + electrode, high cycling stability for over 150 cycles and very good rate performance, >320 mA h g À1 at 2000 mA g À1 .
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.