High resolution SR-FTIR is well suited for characterization of the chemical changes that occur due to thermal damage peripheral to laser incisions in proteinaceous hard tissues. Sub-microsecond pulsed IR lasers resonant with water and mineral absorption bands ablate dentin efficiently with minimal thermal damage. Similar laser parameters are expected to apply to the ablation of alveolar bone.
It is necessary to minimize peripheral thermal damage during laser irradiation, since thermal damage to collagen and mineral compromises the bond strength to restorative materials in dentin and inhibits healing and osteointegration in bone. The overall objective of this study was to test the hypothesis that lasers resonant to the specific absorption of water, collagen, and hydroxyapatite with pulse durations less than the thermal relaxation times at each respective laser wavelength will efficiently remove dentin with minimal peripheral thermal damage. Precise incisions were produced in 3 x 3 mm 2 blocks of human dentin using CO 2 (9.6 µm), Er:YSGG (2.79 µm), and Nd:YAG (355 nm) lasers with and without a computer controlled water spray. Polarization-sensitive optical coherence tomography was used to obtain optical cross-sections of each incision to determine the rate and efficiency of ablation. The peripheral thermal damage zone around each incision was analyzed using polarized light microscopy (PLM) and Synchrotron-Radiation Fourier Transform Infrared Spectro-microscopy (SR-FTIR). Thermally induced chemical changes to both mineral and the collagen matrix was observed with SR-FTIR with a 10-µm spatial resolution and those changes were correlated with optical changes observed with PLM. Minimal (<10-µm) thermal damage was observed for pulse durations less than the thermal relaxation time (T r ) of the deposited laser energy, with and without applied water at 9.6 um and only with applied water at 2.79 µm. For pulse durations greater than T r , significantly greater peripheral thermal damage was observed for both IR laser wavelengths with and without the water spray. There was minimal thermal damage for 355-nm laser pulses, however extensive mechanical damage (cracks) was observed. High resolution SR-FTIR is well suited for characterization of the chemical changes that occur due to thermal damage peripheral to laser incisions in proteinaceous hard tissues. Sub-microsecond pulsed IR lasers resonant with water and mineral absorption bands ablate dentin efficiently with minimal thermal damage. Similar laser parameters are expected to apply to the ablation of alveolar bone.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
customersupport@researchsolutions.com
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
This site is protected by reCAPTCHA and the Google Privacy Policy and Terms of Service apply.
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.