A micromachined specimen with a test section only 150-μm thick was developed for investigating subcritical crack growth in silicon. Crack growth rates in the range 10−4–10−10 m/s were measured as a function of applied stress intensity (v–K curves) during tests in humid air and dry nitrogen lasting up to 24 h. The fracture toughness, KIc of {110} silicon was also measured at 1.15 ± 0.08 MPa m1/2. While some evidence MPa-m1/2 of subcritical crack growth appeared to occur in the region 0.9 KIc < K > 0.98 KIc, the extremely high crack growth exponent (n 100) and the high ratio of the apparent stress corrosion threshold, KIscc, to the fracture toughness, KIscc/KIc > 0.9, suggests that no clear evidence exists for a stress corrosion process in silicon exposed to humid air.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.